Wear Behavior of Biodegradable Mg–5Zn–1Y–(0–1)Ca Magnesium Alloy in Simulated Body Fluid

verfasst von: Asma Ghanbari, Hassan Jafari, Faramarz Ashenai Ghasemi

Erschienen in: Metals and Materials International | Ausgabe 3/2020

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

In this study, wear behavior of biodegradable Mg–5Zn–1Y–(0–1)Ca alloys is investigated in simulated body fluid. Wear test is performed using a pin-on-disc system, under three different loads of 10, 20 and 40 N, at ambient temperature; and the whole configuration is exposed to simulated body fluid. The volumetric wear rate and friction coefficient of each alloy are determined. The worn surfaces are analyzed using a scanning electron microscope, equipped with an energy dispersive spectrometer to determine the involved main wear mechanism. The Ca-free alloy contains α-Mg and intermetallic Mg3YZn6, and Ca addition produces another intermetallic Ca2Mg6Zn3. Results show that different wear mechanisms and rates, as well as friction coefficients, are achieved due to the effect of simulated body fluid on the alloys with regards to the different Ca content and the presence of corrosion products. Microscopic studies reveal that abrasion is the dominant wear mechanism taken place in all alloys under all loads. Increasing Ca content leads to wear resistance deterioration while increasing wear load results in decreasing wear rate and friction coefficient of the alloys. The results of the wear rate and friction coefficient of Mg–5Zn–1Y–1Ca alloy exhibit greater instability compared to the other alloys due to its more enhanced corrosion caused by the formation of the intermetallic Ca2Mg6Zn3 particles. In total, Ca-free alloy provides the best wear resistance, especially at the higher wear load.

Graphical Abstract

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat L. Cui, L. Sun, R. Zeng, Y. Zheng, S. Li, Sci. China Mater. 61, 607 (2018) L. Cui, L. Sun, R. Zeng, Y. Zheng, S. Li, Sci. China Mater. 61, 607 (2018)
2.
Zurück zum Zitat K.K. Ajith Kumar, U.T.S. Pillai, B.C. Pai, M. Chakraborty, Met. Mater. Int. 19, 1167 (2013) K.K. Ajith Kumar, U.T.S. Pillai, B.C. Pai, M. Chakraborty, Met. Mater. Int. 19, 1167 (2013)
3.
Zurück zum Zitat L. Tonelli, P. Dolcet, M. Dabal, C. Martini, Wear 404–405, 122 (2018) L. Tonelli, P. Dolcet, M. Dabal, C. Martini, Wear 404–405, 122 (2018)
4.
Zurück zum Zitat S. Koleini, M. Hasbullah Idris, H. Jafari, Mater. Des. 33, 20 (2012) S. Koleini, M. Hasbullah Idris, H. Jafari, Mater. Des. 33, 20 (2012)
5.
Zurück zum Zitat F. Qin, G. Xie, Z. Dan, Sh Zhu, I. Seki, Intermetallics 42, 9 (2013) F. Qin, G. Xie, Z. Dan, Sh Zhu, I. Seki, Intermetallics 42, 9 (2013)
6.
7.
Zurück zum Zitat J.Z. Ilich, J.E. Kerstetter, J. Am. Coll. Nutr. 19, 715 (2000) J.Z. Ilich, J.E. Kerstetter, J. Am. Coll. Nutr. 19, 715 (2000)
8.
Zurück zum Zitat F. Witte, V. Kaese, H. Haferkamp, E. Switzer, A. Meyer-Lindenberg, C.J. Wirth, Biomaterials 26, 3557 (2005) F. Witte, V. Kaese, H. Haferkamp, E. Switzer, A. Meyer-Lindenberg, C.J. Wirth, Biomaterials 26, 3557 (2005)
9.
Zurück zum Zitat A. Madhan Kumar, S. Fida Hassan, A.A. Sorour, M. Paramsothy, M. Gupta, Met. Mater. Int. 25, 105 (2009) A. Madhan Kumar, S. Fida Hassan, A.A. Sorour, M. Paramsothy, M. Gupta, Met. Mater. Int. 25, 105 (2009)
10.
Zurück zum Zitat N. Li, Y. Zheng, J. Mater. Sci. Technol. 29, 489 (2013) N. Li, Y. Zheng, J. Mater. Sci. Technol. 29, 489 (2013)
11.
Zurück zum Zitat B. Zhang, Y. Hou, X. Wang, Y. Wang, L. Geng, Mater. Sci. Eng. C 31, 1667 (2011) B. Zhang, Y. Hou, X. Wang, Y. Wang, L. Geng, Mater. Sci. Eng. C 31, 1667 (2011)
12.
Zurück zum Zitat R. Erbel, C. Di Mario, J. Bartunek, J. Bonnier, B. de Bruyne, F.R. Eberli, P. Erne, M. Haude, B. Heublein, M. Horrigan, C. Ilsley, D. Bose, J. Koolen, T.F. Luscher, N. Weissman, R. Waksman, Lancet 369, 1869 (2007) R. Erbel, C. Di Mario, J. Bartunek, J. Bonnier, B. de Bruyne, F.R. Eberli, P. Erne, M. Haude, B. Heublein, M. Horrigan, C. Ilsley, D. Bose, J. Koolen, T.F. Luscher, N. Weissman, R. Waksman, Lancet 369, 1869 (2007)
13.
Zurück zum Zitat B. Smola, L. Joska, V. Březina, I. Stulíková, F. Hnilica, Mater. Sci. Eng. C 32, 659 (2012) B. Smola, L. Joska, V. Březina, I. Stulíková, F. Hnilica, Mater. Sci. Eng. C 32, 659 (2012)
14.
Zurück zum Zitat H. Tapiero, K.D. Tew, Biomed. Pharmacother. 57, 399 (2003) H. Tapiero, K.D. Tew, Biomed. Pharmacother. 57, 399 (2003)
15.
Zurück zum Zitat L. Cizek, S. Rusz, O. Hilser, R. Śliwa, D. Kuc, T. Tanski, M. Tikocz, Arch. Metall. Mater. 62, 2365 (2017) L. Cizek, S. Rusz, O. Hilser, R. Śliwa, D. Kuc, T. Tanski, M. Tikocz, Arch. Metall. Mater. 62, 2365 (2017)
16.
Zurück zum Zitat S. Cai, T. Lei, N. Li, F. Feng, Mater. Sci. Eng. C 32, 2570 (2012) S. Cai, T. Lei, N. Li, F. Feng, Mater. Sci. Eng. C 32, 2570 (2012)
17.
Zurück zum Zitat S. Zhang, X. Zhang, C. Zhao, J. Li, Y. Song, C. Xie, H. Tao, Y. Zhang, Y. He, Y. Jiang, Y. Bian, Acta Biomater. 6, 626 (2010) S. Zhang, X. Zhang, C. Zhao, J. Li, Y. Song, C. Xie, H. Tao, Y. Zhang, Y. He, Y. Jiang, Y. Bian, Acta Biomater. 6, 626 (2010)
18.
Zurück zum Zitat Y. Sun, B. Zhang, Y. Wang, L. Geng, X. Jiao, Mater. Des. 34, 58 (2012) Y. Sun, B. Zhang, Y. Wang, L. Geng, X. Jiao, Mater. Des. 34, 58 (2012)
19.
Zurück zum Zitat Y. Jang, Z. Tan, Ch. Jurey, Zh Xu, Zh Dong, B. Collins, Y. Yun, J. Sankar, Mater. Sci. Eng. C 48, 28 (2015) Y. Jang, Z. Tan, Ch. Jurey, Zh Xu, Zh Dong, B. Collins, Y. Yun, J. Sankar, Mater. Sci. Eng. C 48, 28 (2015)
20.
Zurück zum Zitat V. Neubert, I. Stulíková, B. Smola, B.L. Mordike, M. Vlach, A. Bakkar, J. Pelcová, Mater. Sci. Eng. A 462, 329 (2007) V. Neubert, I. Stulíková, B. Smola, B.L. Mordike, M. Vlach, A. Bakkar, J. Pelcová, Mater. Sci. Eng. A 462, 329 (2007)
21.
Zurück zum Zitat E. Zhang, W. He, H. Du, K. Yang, Mater. Sci. Eng. A 488, 102 (2008) E. Zhang, W. He, H. Du, K. Yang, Mater. Sci. Eng. A 488, 102 (2008)
22.
Zurück zum Zitat S. Naghdali, H. Jafari, M. Malekan, Thermochim. Acta 667, 50 (2018) S. Naghdali, H. Jafari, M. Malekan, Thermochim. Acta 667, 50 (2018)
23.
Zurück zum Zitat MZh Ge, J.Y. Xiang, Y. Tang, X. Ye, Z. Fan, Y.L. Lu, X.H. Zhang, Surf. Coat. Technol. 337, 501 (2018) MZh Ge, J.Y. Xiang, Y. Tang, X. Ye, Z. Fan, Y.L. Lu, X.H. Zhang, Surf. Coat. Technol. 337, 501 (2018)
24.
Zurück zum Zitat J. An, R.G. Li, Y. Lu, C.M. Chen, Y. Xu, X. Chen, L.M. Wang, Wear 265, 97 (2008) J. An, R.G. Li, Y. Lu, C.M. Chen, Y. Xu, X. Chen, L.M. Wang, Wear 265, 97 (2008)
25.
Zurück zum Zitat Y. Niu, R. Cui, Y. He, Z. Yu, J. Alloys Compd. 610, 294 (2014) Y. Niu, R. Cui, Y. He, Z. Yu, J. Alloys Compd. 610, 294 (2014)
26.
Zurück zum Zitat D.B. Liu, B. Wu, X. Wang, M.F. Chen, Rare Met. 34, 553 (2015) D.B. Liu, B. Wu, X. Wang, M.F. Chen, Rare Met. 34, 553 (2015)
27.
Zurück zum Zitat H. Somekava, A. Shimoda, T. Hirayama, T. Matsuoka, T. Mukai, Mater. Trans. 55, 216 (2014) H. Somekava, A. Shimoda, T. Hirayama, T. Matsuoka, T. Mukai, Mater. Trans. 55, 216 (2014)
28.
Zurück zum Zitat N.N. Aung, W. Zhou, L.E.N. Lim, N.N. Aung, W. Zhou, L.E.N. Lim, Wear 265, 780 (2008) N.N. Aung, W. Zhou, L.E.N. Lim, N.N. Aung, W. Zhou, L.E.N. Lim, Wear 265, 780 (2008)
29.
Zurück zum Zitat C. Taltavull, P. Rodrigo, B. Torres, A.J. López, J. Rams, Mater. Des. 56, 549 (2014) C. Taltavull, P. Rodrigo, B. Torres, A.J. López, J. Rams, Mater. Des. 56, 549 (2014)
30.
Zurück zum Zitat C. Taltalvull, B. Torres, A.J. López, J. Rams, Wear 301, 615 (2013) C. Taltalvull, B. Torres, A.J. López, J. Rams, Wear 301, 615 (2013)
31.
Zurück zum Zitat H. Li, D.B. Liu, Y. Zhao, F. Jin, M.F. Chen, J. Mater. Eng. Perform. 25, 3890 (2016) H. Li, D.B. Liu, Y. Zhao, F. Jin, M.F. Chen, J. Mater. Eng. Perform. 25, 3890 (2016)
32.
Zurück zum Zitat H. Jafari, F. Rahimi, Z. Sheikhsofla, Mater. Corros. 67, 396 (2015) H. Jafari, F. Rahimi, Z. Sheikhsofla, Mater. Corros. 67, 396 (2015)
33.
Zurück zum Zitat M.L. Hu, Q.D. Wang, C.J. Chen, D.D. Yin, W.J. Ding, Z.S. Ji, Mater. Des. 42, 223 (2012) M.L. Hu, Q.D. Wang, C.J. Chen, D.D. Yin, W.J. Ding, Z.S. Ji, Mater. Des. 42, 223 (2012)
34.
Zurück zum Zitat G. Peitao, T. Mingyang, Z. Chaoyang, Surf. Coat. Technol. 359, 197 (2019) G. Peitao, T. Mingyang, Z. Chaoyang, Surf. Coat. Technol. 359, 197 (2019)
35.
Zurück zum Zitat J. Dai, X. Zhang, Q. Yin, Sh Ni, Zh Ba, Zh Wang, J. Magn. Alloy 5, 448 (2017) J. Dai, X. Zhang, Q. Yin, Sh Ni, Zh Ba, Zh Wang, J. Magn. Alloy 5, 448 (2017)
36.
Zurück zum Zitat A. Somi Reddy, B.N. Pramila Bai, K.S.S. Murthy, S.K. Biswas, Wear 181–183, 658 (1995) A. Somi Reddy, B.N. Pramila Bai, K.S.S. Murthy, S.K. Biswas, Wear 181–183, 658 (1995)
37.
Zurück zum Zitat B.N. Pramila Bai, S.K. Biswas, Acta Metall. Mater. 39, 833 (1991) B.N. Pramila Bai, S.K. Biswas, Acta Metall. Mater. 39, 833 (1991)
38.
Zurück zum Zitat N.V. Phuong, B.R. Fazli, S. Moon, Met. Mater. Int. 23, 106 (2017) N.V. Phuong, B.R. Fazli, S. Moon, Met. Mater. Int. 23, 106 (2017)
39.
Zurück zum Zitat M. Bornapour, M. Celikin, M. Cerruti, M. Pekguleryuz, Mater. Sci. Eng. C 35, 267 (2014) M. Bornapour, M. Celikin, M. Cerruti, M. Pekguleryuz, Mater. Sci. Eng. C 35, 267 (2014)
40.
Zurück zum Zitat V. Kumar, L. Li, H. Gui, X. Wang, Q.X. Huang, Q.Y. Li, F. Mokdad, D. Chen, D.Y. Li, Wear 414–415, 126 (2018) V. Kumar, L. Li, H. Gui, X. Wang, Q.X. Huang, Q.Y. Li, F. Mokdad, D. Chen, D.Y. Li, Wear 414–415, 126 (2018)
41.
Zurück zum Zitat F. Muhaffel, H. Cimenoglu, Surf. Coat. Technol. 357, 822 (2019) F. Muhaffel, H. Cimenoglu, Surf. Coat. Technol. 357, 822 (2019)
42.
Zurück zum Zitat F. Doost Mohammadi, H. Jafari, Trans. Nonferr. Met. Soc. China 28, 2199 (2018) F. Doost Mohammadi, H. Jafari, Trans. Nonferr. Met. Soc. China 28, 2199 (2018)
Metadaten
Titel
Wear Behavior of Biodegradable Mg–5Zn–1Y–(0–1)Ca Magnesium Alloy in Simulated Body Fluid
verfasst von
Asma Ghanbari
Hassan Jafari
Faramarz Ashenai Ghasemi
Publikationsdatum
20.06.2019
Verlag
The Korean Institute of Metals and Materials
Erschienen in
Metals and Materials International / Ausgabe 3/2020
Print ISSN: 1598-9623
Elektronische ISSN: 2005-4149
DOI
https://doi.org/10.1007/s12540-019-00330-2

Weitere Artikel der Ausgabe 3/2020

Metals and Materials International 3/2020 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.