Wide Structural and Magnetic Successive Transitions and Related Magnetocaloric Properties in a Directionally Solidified Polycrystalline Ni–Co–Mn–In Alloy

Shape Memory and Superelasticity > Ausgabe 1/2020
F. Chen, J. L. Sánchez Llamazares, C. F. Sánchez-Valdés, P. Müllner, Y. X. Tong, L. Li
Wichtige Hinweise
This article is an invited submission to Shape Memory and Superelasticity selected from presentations at the International Conference on Ferromagnetic Shape Memory Alloys (ICFSMA) held June 2–7, 2019 in Prague, Czech Republic, and has been expanded from the original presentation.

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.


We fabricated a Ni45Co6.4Mn37In11.6 polycrystalline sample with a specific texture by directional solidification. The alloy is characterized by wide successive structural and magnetic phase transitions that considerably extend their temperature intervals with the increase in the applied magnetic field. Under a magnetic field change μoΔH of 5 T, the working temperature window obtained from the magnetic entropy change curve for the structural and magnetic transition is as large as 66 and 52 K, respectively. As a result, the corresponding refrigeration capacity RC reached high values of 118 and 95 J kg−1, respectively, irrespective of the considerably small magnetic entropy changes.

Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten

Über diesen Artikel

Weitere Artikel der Ausgabe 1/2020

Shape Memory and Superelasticity 1/2020 Zur Ausgabe

Premium Partner


    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.