Formation of a KNbO₃ single crystal using solvothermally synthesized K_2-mNb₂O_6-m/2 pyrochlore phase

A K_2-mNb₂O_6-m/2 single crystal with a pyrochlore phase formed when the Nb₂O₅ + x mol% KOH specimens with 0.6 ≤ x ≤ 1.2 were solvothermally heated at 230 °C for 24 h. They have an octahedral shape with a size of 100 μm, and the composition of this single crystal is close to K_1.3Nb₂O_5.65. The single-crystal KNbO₃ formed when the single-crystal K_2-mNb₂O_6-m/2 was annealed at a temperature between 600 °C and 800 °C with K₂CO₃ powders. When annealing was conducted at 600 °C (or with a small amount of K₂CO₃), the KNbO₃ single crystal has a rhombohedral structure that is stable at low temperatures (< − 10 °C). The formation of the rhombohedral KNbO₃ structure can be explained by the presence of the K⁺ vacancies in the specimen. The KNbO₃ single crystal with an orthorhombic structure formed when the K_2-mNb₂O_6-m/2 single crystal was annealed at 800 °C with 20 wt% of K₂CO₃.