Microstructure and H₂S gas sensing properties of nanocrystalline perovskite-type La_0.6Co_0.4Mn_0.5Ni_0.5O₃

Nanocrystalline La_1−x Co _x Mn_1−y Ni _y O₃ (x = 0.2 and 0.4; y = 0.1, 0.3, and 0.5) thick films sensors prepared by sol–gel method were studied for their H₂S gas sensitivity. The structural and morphological properties have been carried out by X-ray diffraction (XRD) and transmission electron microscopy (TEM). Average particle size estimated from XRD and TEM analyses was observed to be 30–35 nm. The gas response characteristics were found to depend on the dopants concentration and operating temperature. The maximum H₂S gas response of pure LaMnO₃ was found to be at 300 °C. In order to improve the gas response, material doped with transition metals Co and Ni on A- and B-site, respectively. The La_0.6Co_0.4Mn_0.5Ni_0.5O₃ shows high response towards H₂S gas at an operating temperature 250 °C. The Pd-doped La_0.6Co_0.4Mn_0.5Ni_0.5O₃ sensor was found to be highly sensitive to H₂S at an operating temperature 200 °C. The gas response, selectivity, response time and recovery time were studied and discussed.