The effects of thermomechanical treatments on crystallographic texture and grain size evolution and their impact on the pseudoelastic properties in Fe41–Ni28–Co17–Al11.5–Ti2.5 (at.%) were studied in the present paper. The results show that cold rolling leads to brass-type texture in this alloy, which is typical for low stacking fault energy materials. Thermal treatments up to 1300 °C were conducted and it is shown that the presence of β-phase helps to control grain growth. After the dissolution of the secondary phase induced by heat treatment at higher temperatures, a strong {230}〈001〉 recrystallization texture evolves in cold rolled samples already upon imposing medium reduction ratios. Finally, good pseudoelastic properties are found in conditions being characterized by adequate texture and grain sizes spanning over the entire thickness of the samples tested.
Notes
This invited article is part of a special issue of Shape Memory and Superelasticity to honor Prof. Dr.-Ing. Gunther Eggeler. This special issue was organized by Prof. Hüseyin Sehitoglu, University of Illinois at Urbana-Champaign, and Prof. Dr.-Ing. Hans Jürgen Maier, Leibniz Universität Hannover.
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Introduction
Shape memory alloys (SMAs) have gained increasing attention due to their unique properties, i.e. shape memory effect and pseudoelasticity (PE) [1]. Among numerous SMA systems, binary Ni–Ti is currently the most widely studied alloy system [2, 3]. Furthermore, Ni–Ti is used in industrial applications since decades. However, high costs related to complex processing and alloying elements limit its use to niche applications. Thus, due to their low cost and excellent cold workability the development of Fe-based SMAs came into focus of research during the past two decades [1]. However, the inherently non-thermoelastic character of the martensitic transformation (MT) in ferrous SMAs, e.g. Fe–Mn and Fe–Mn–Si, has been a roadblock towards obtaining adequate PE behavior [4, 5].
Recently, two very promising alloy systems in this class of SMAs showing room temperature PE were discovered, Fe–Ni–Co–Al–Ta–B in 2010 [6] and Fe–Mn–Al–Ni in 2011 [7]. Since then, many research efforts have been made focusing on the Fe–Ni–Co–Al–X (FNCAX) (X = Ta, Ti, Nb) and Fe–Mn–Al–Ni–X (X = Ti, Cr) SMA systems to improve PE in single- and polycrystalline conditions. In case of FNCAX, the functional properties are based on the MT between the disordered parent γ-(fcc) and the martensitic α′-phase (bct) [8‐12]. In these alloys, secondary phases play a key role in designing mechanical properties. Obtaining a thermoelastic character of the MT in FNCAX is strongly related to the presence of coherent, ordered γ′-(L12) precipitates of Ni3Al-type [9]. Due to the formation of coherency stress fields, these fine dispersed precipitates mechanically strengthen the matrix of the parent phase [7, 13]. However, the formation of the β-NiAl (B2) phase, particularly along grain boundaries, evokes pronounced brittleness deteriorating the mechanical properties [14, 15].
Advertisement
In addition to the role of secondary phases, in polycrystalline structures several microstructural characteristics, i.e. grain size, orientation distribution and texture, respectively, have a significant impact on the functional and structural properties of FNCAX SMAs [14, 15]. The relationship between crystal orientation, crystallographic texture and PE is well understood for Fe–Ni–Co–Al–Ta(–B) [6, 9], Fe–Ni–Co–Al–Nb(–B) [16] and other alloys belonging to the FNCAX family [13, 14, 17]. For the polycrystalline FNCAX SMAs, all of them containing Boron as an element suppressing the evolution of the β-phase, cold rolling followed by recrystallization is a well-established approach to obtain an excellent PE response in the polycrystalline condition [7]. However, to obtain an appropriate recrystallization texture, i.e. {hkl}〈100〉 in the γ-phase, crucially needed for superior functional performance, the deformation degree during cold rolling is an important factor. Many studies have confirmed that a cold rolling reduction above 98% should be achieved to robustly promote {hkl}〈100〉 recrystallization textures [1, 12, 17, 18]. Nevertheless, Lee et al. [17] found that PE could already be obtained in thicker sheets, i.e. following a reduction of 90% only during cold rolling.
In light of these findings, in the present work the influence of various reduction ratios during cold rolling ranging from 85% to 92% as well as post-process heat treatments on recrystallization texture and grain size evolution in Fe–Ni–Co–Al–Ti SMA (without any addition of Boron) has been studied. Incremental strain tests have been conducted at room temperature to study the functional properties under pseudoelastic loading. Results obtained are used to establish solid relationships between the functional properties following thermomechanical processing and related texture evolution as well as the influence of β-phase in grain growth control.
Experimental Procedure
A polycrystalline Fe41–Ni28–Co17–Al11.5–Ti2.5 (at.%) SMA produced using vacuum induction melting was investigated in this study. Specimens with 20 mm thickness were cut from the cylindrical as-cast ingots and homogenized at 1150 °C for 4 h under argon flow followed by water quenching. Specimens were cold rolled without intermediate annealing with different reduction ratios, i.e. 85%, 90% and 92% (85, 90 and 92 in the reminder of the text) leading to final sheet thicknesses of 1.4 mm, 0.9 mm and 0.8 mm, respectively. For microstructure analysis and mechanical testing small specimens as well as dog-bone-shaped samples with a gauge length of 18 mm were electro-discharged machined (EDM) from the cold rolled sheets. To study the impact of recrystallization temperatures on texture and grain size evolution heat treatments were conducted for 0.5 h at three different maximum temperatures, as highlighted in Fig. 1, followed by water quenching. During the heat treatments samples were kept in quartz tubes under argon atmosphere to avoid oxidation.
Fig. 1
Thermal treatments conducted in this study with the three different maximum temperatures 1300 °C, 1250 °C and 1200 °C
×
For microstructure characterization optical microscopy (OM), scanning electron microscopy (SEM) including electron backscatter diffraction (EBSD) and X-ray diffraction were conducted. Specimens were ground down to 5 µm grit size and mechanically polished for 2 h using a colloidal silica suspension (0.04 µm) employing a VibroMet 2 vibratory polishing machine. For OM, specimens were etched using 2% nitric acid solution. SEM analysis was conducted using Zeiss ULTRA GEMINI high-resolution SEM operated at an accelerating voltage of 20 kV. X-ray pole figures and diffractograms were determined using a Seifert Analytical X-ray diffractometer with a Mn tube (Kα1/Kα2 lines) and a monochromator at 35 kV and 30 mA. To analyse texture evolution following the different recrystallization treatments (cf. Fig. 1), pole figures from the three main peaks of the γ-phase were measured and the orientation distribution function (ODF) was calculated using the Mtex Package [19].
Advertisement
In order to evaluate the PE properties, quasi-static uniaxial tensile incremental strain tests (ISTs) were conducted using a servo-hydraulic test rig at ambient temperature. ISTs were carried out at a nominal strain rate of 0.33 × 10–3 s−1 in displacement control. Strains were determined using an extensometer with 12 mm gauge length. For mechanical testing, samples were additionally aged at 600 °C for 4 h to precipitate the γ′-phase. Following aging, samples were again mechanically ground.
Results and Discussion
Grain Size and Phase Evolution
Figure 2 shows the microstructure of Fe–Ni–Co–Al–Ti cold rolled material following three different reduction ratios. All conditions are characterized by the presence of γ- and β-phase. As will be highlighted in the following, all measurements conducted in present work using different techniques (X-ray, OM and EBSD) did not reveal the presence of martensite in any specimen following cold rolling. An explanation for this observation could be deduced from the martensite transformation temperatures that are reported to be below 270 K for several alloys belonging to this family of SMAs. The low transformation temperatures are thought to be responsible for pronounced dislocation activity and the absence of martensitic transformation, however, in-depth analysis is out of the scope of present work. In line with results presented here, however, no martensite after cold rolling was shown in the literature reporting on similar alloys. The β-phase is oriented alongside the rolling direction (RD) being characterized by elongated grains and the typical “pancake” shape. However, grain morphology of the γ-phase, i.e. size and shape, as a function of deformation level is not clearly evident from OM analysis. In addition, EBSD inverse pole figure (IPF) maps of the cold rolled specimens were obtained and are displayed in Fig. 3. As can be seen, independent of the deformation degree, grain sizes are in a wide range between 3 µm and 10 µm due to fragmentation resulting from mechanical processing. The ND plane was chosen for EBSD analysis to facilitate evaluation of grain size evolution. Clearly, intensity of texture increases with increasing reduction ratio. The evolution of the main orientations will be discussed in the next section.
Fig. 2
Optical micrographs of cold rolled specimens with reduction of i, iv 85%; ii, v 90% and iii, vi 92% (RD is vertical)
Fig. 3
EBSD inverse pole figure (IPF) maps of cold rolled specimens with reduction ratio of i 85%, ii 90% and iii 92%. The IPF maps were plotted with respect to the normal direction (ND). The color-coded standard triangle and the reference coordinate system are shown in (i) and (iii), respectively (RD is vertical) (Color figure online)
×
×
As the microstructures shown are highly unfavorable for enhanced functional performance, thermal treatments (TT) at 1300 °C, 1250 °C and 1200 °C were performed to study the grain size and texture evolution upon recrystalization. It is important to note that the grain boundary (GB) movement of those GBs that are decorated by secondary phase can be decreased due to pinning forces and, thereby, grain growth is impeded [20]. This phenomenon has been reported for various SMAs, e.g. Cu-based [21], Co–Ni–Ga [22] and FNCAX [12, 17], whereas the β-phase is present in the latter case. Maximum temperatures of TT were chosen to be close to the dissolution temperature of the β-phase. For Fe–30Ni–15Co–10Al–2.5Ti–0.05B (at.%) Lee et al [17]. showed that the alloys are in single γ-phase condition upon TT at 1200 °C. Figure 4 shows the diffractograms for specimens rolled to 92% in the as-rolled (Fig. 4i) and recrystallized conditions following TT at 1200 °C, TT at 1250 °C and TT at 1300 °C (Fig. 4ii–iv), respectively. As the material is characterized by a similar phase evolution in the as-rolled and heat-treated conditions after cold rolling with reduction ratios of 85% and 90%, these results are not shown in present work for the sake of brevity. As can be seen in Fig. 4ii), for the Fe–Ni-Co–Al–Ti SMA being used in the present study β-phase is still present after cooling from the TT at 1200 °C. However, a significant change in peak intensities of the γ- and β-phase is evident compared to the as-rolled condtion, especially in case of the (220) γ-peak located at 2θ = 111°. Thus, according to the diffractogram (Fig. 4ii), the volume fraction of the secondary phase is significantly decreased. Additional analysis using OM (not shown here) revealed values close to 5%. After the TT at 1250 °C the β-phase is almost fully dissolved within the matrix, nevertheless, there is still some small amount mostly located at the grain boundaries as can be seen in the 2nd column of Fig. 5. Upon TT at 1300 °C no traces of the β-phase are left. This clearly indicates that the absence of Boron leads to a slight increase of dissolution temperature for the composition investigated in this study.
Fig. 4
X-ray diffractograms of specimens rolled with a reduction ratio of 92% in different conditions: i cold rolled, ii TT-1200 °C, iii TT-1250 °C and iv TT-1300 °C
Fig. 5
EBSD IPF maps in the ND plane of all conditions after thermal treatments. The color-coded standard triangle and the reference coordinate system are shown in Fig. 3. RD is vertical. Scale bars are different for the conditions considered (Color figure online)
×
×
When the β-phase is dissolved into the matrix, pinning forces that imped grain growth of the γ-phase are diminished [17]. Figure 5 shows EBSD IPF maps for the 85, 90 and 92 specimens in the thermally treated conditions. Independent of the reduction ratio during cold rolling, the EBSD plots illustrate an increase in grain size with increasing annealing temperature. In line with the findings obtained by X-ray diffraction, following the TT at 1200 °C the presence of β-phase is visible and exemplarily marked by a black arrow (1st column of Fig. 5), whereas only small amounts of β-phase remain in the microstructure after the TT at 1250 °C (2nd column of Fig. 5). Finally, following the TT at 1300 °C (3rd column of Fig. 5) the β-phase is completely dissolved promoting secondary recrystallization of the γ-phase leading to grain sizes up to 5 mm. In conclusion, by an appropriate choice of the annealing temperatures and time, grain growth can be robustly applied for adjusting mechanical properties of the FNCAX SMA.
Texture Evolution
Figure 6 shows ODF sections for φ2 = 0°, 45° and 65° related to the γ-phase for the 85, 90 and 92 specimens in the as-rolled condition. It is known from literature that fcc materials can feature different types of rolling textures, depending on material and processing parameters as well as stacking fault energy [23]. One common type of rolling texture is the so-called Brass-type texture. It can be described as a combination of Brass-{110}〈112〉 and Goss-{110}〈001〉 orientations along the α-fiber, where 〈110〉 is parallel to the normal direction (ND) of the rolled sheet [23]. As can be deduced from Figs. 2 and 3 the microstructure of the as-rolled specimens is characterized by the fragmentation of the γ-grains due to the rolling process. The X-ray analysis in Fig. 6 reveals for all as-rolled conditions that the resulting texture is Brass-type, being common for low-SFE materials, e.g. FNCAX SMAs [12]. In Fig. 3 the majority of grains is characterized by the 〈110〉γ direction being parallel to the ND direction. This result is in good agreement with the definition of the α-fiber. However, for all studied deformation ratios a slight change in orientation density can be observed with increasing reduction ratio from 85% to 92%. This is associated to the increase of the {110}〈115〉γ Goss/Brass (see Fig. 6iii) orientation, which has been previously reported as an intermediate texture that appears previously to the full brass texture in conditions featuring a high reduction ratio [18].
Fig. 6
ODF sections for φ2 = 0°, 45° and 65° for cold rolled specimens with reduction ratios of i 85%, ii 90% and iii 92%. (Orientation {110}〈115〉γ is marked with ° in iii) (Color figure online)
×
In Fig. 7 ODF sections for the γ-phase are illustrated for specimens heat treated according to TT-1250 °C. As can be seen in the X-ray diffractogram shown in Fig. 4 and the EBSD images shown in Fig. 5 following the TT at 1250 °C, the β-phase still is present in the microstructure, particularly alongside the GBs. As previously discussed, the main phase, i.e. the γ-phase, thus, has not been fully recrystallized. Grain size is around 50 µm for a reduction ratio of 85% and close to 200 µm for the reduction ratios of 90% and 92% (cf. Fig. 5). In addition, the main texture component remains in the α-fiber, however, with a remarkable increase of the Goss/Brass orientation for all TT-1250 °C specimens. The significant increase of the ODF density intensities is also reflected in the remarkable change of the (220)γ peak between the as-rolled and subsequently heat-treated condition shown in the diffractograms in Fig. 4i and iii, respectively. Furthermore, grain sizes and the intensity of the main orientation increase with increasing reduction ratio (cf. 2nd column in Figs. 5 and 7). This is related to the stored energy imposed by the deformation process of the material. Texture evolution during the TT at 1200 °C is very similar and, thus, not shown in the present paper for the sake of brevity.
Fig. 7
ODF sections for φ2 = 0°, 45° and 65° for specimens heat treated according to TT-1250 °C subsequent to cold rolling with reduction ratios of i 85%, ii 90% and iii 92% (Color figure online)
×
Figure 8 shows the ODFs for specimens heat treated according to the TT-1300 °C. Annealing at this temperature results in the full dissolution of the β-phase (cf. Fig. 4iv and the 3rd column of Fig. 5). Due to the absence of the secondary phase, there is no pinning force that could impede the secondary recrystallization and, thus, grains grow up to 5 mm as can be seen in Fig. 5. In addition, a fundamental change of the texture component occurs during the recrystallization process at 1300 °C as compared to microstructure evolution upon TT at 1200 °C and TT at 1250 °C. In detail, the α-fiber vanishes and is replaced by the {hkl}〈100〉γ type component, where the 〈100〉 direction is parallel to RD. For the specimen being characterized by a reduction ratio of 92%, the texture main component is Goss-{110}〈001〉γ, whereas for both 85 and 90 specimens the main component is close to {230}〈001〉. This texture evolution is in good agreement with previous results observed by various authors [12‐14, 18]. However, texture intensities reported in this paper are higher than the ones obtained in previous works when looking at similar reduction ratios. This difference might, at least in part, result from the relative slow heating to the maximum temperature during the TT allowing for well-defined development of recrystallized grains in the material.
Fig. 8
ODF sections for φ2 = 0°, 45° and 65° for specimens heat-treated according to TT-1300 °C following cold rolling with reduction ratios of i 85%, ii 90% and iii 92%. ({230}〈001〉 is marked with + in ii and Goss Orientation is marked with ° in iii) (Color figure online)
×
Pseudoelasticity
Samples treated according to TT-1250 °C and TT-1300 °C were aged at 600 °C for 4 h to induce γ′-phase precipitates. Besides the influence of texture, the size and the volume fraction of the γ′-phase play an important role in phase transformation as both affect the morphology of the martensite and eventually the amount of irreversible deformation following pseudoelastic testing [9, 13]. Figure 9 shows the pseudoelastic response at room temperature for the specimens treated according to TT-1250 °C and TT-1300 °C (RD is parallel to load direction). As can be seen in Fig. 9v, the transformation stress is close to 500 MPa and a fully reversible MT is obtained for the specimen being characterized by a reduction ratio of 90% following the TT at 1300 °C. Nevertheless, the specimen failed after 1.5% of deformation, which could probably be attributed to remaining high angle grain boundaries as was suggested by Lee et al. [17]. These grain boundaries can result in a brittle material behavior and, thus, to early fracture. The EBSD results in Fig. 5 support this assumption, as the microstructure still contains some grains being characterized by unfavorable crystallographic orientation. The 85 and 92 specimens after TT at 1300 °C show no PE effect upon deformation. The transformation stress for a reduction ratio of 92% is around 800 MPa and the sample with the reduction ratio of 85% already failed in the elastic regime. The difference in mechanical response can be related to grain constraints being present due to grains lacking adequate crystallographic orientation. Since the aging treatments were done in the same way throughout all tests, aging affected changes in the mechanical response can be excluded. So far, data reported in the literature revealed that only very specific material conditions are characterized by good PE properties in case of the FNCAX SMAs. Only thermomechanically processed conditions being characterized by pronounced texture and grain sizes up to 2 mm, spanning over the entire thickness of the samples, showed a fully reversible phase transformation [17]. This kind of microstructure helps suppressing grain constrains in the sample volume, since every single grain is solely constraint in a 2D space. Upon TT-1300 °C the grain size grows up to more than 3 mm and, thus, spans over the entire thickness of the samples tested. In addition, as can be seen on ODF sections in Fig. 8, the texture in specimens changes from {230}〈001〉 orientation upon reduction of 85% and 90% to Goss in the 92% condition. The {230}〈001〉 was previously reported to be a beneficial texture for PE [12] while there as is no references in the literature reporting on good PE response for pure Goss texture. Finally, the intensities of the main orientations in the 90% specimens are higher than in 85%. In consequence, only in the TT-1300 °C condition (reduction ratio of 90%) the grain orientation as well as grain size seem to precisely fulfil the prerequisites for reversible functional properties.
Fig. 9
Pseudoelastic response of specimens upon treatment according to TT-1250 °C (i–iii) and TT-1300 °C (iv–vi) subsequently aged at 600 °C for 4 h (RD parallel to load direction)
×
As is revealed in Fig. 5, upon TT at 1250 °C unfavorable oriented grains may lead to significant grain constraints, however, the fraction of unfavorable grains is lower for 90/TT-1250 °C and 92/TT-1250 °C conditions. This might explain the differences in the mechanical response for the sample featuring a reduction ratio of 85%. In this condition a very early fracture is observed, similar to the 85/TT-1300 °C condition. For both the 90 and 92 specimens following the TT at 1250 °C at least minor PE behavior is seen. Stresses for MT in these conditions are significantly higher as compared to the TT-1300 °C conditions featuring the same reduction ratios. Since the ODF sections of the TT-1250 °C conditions reveal a high density of Goss/Brass texture with a majority of {110} planes parallel to the ND plane and the 〈115〉 directions parallel to rolling direction, a possible explanation for the higher stresses for MT can be deduced. According to [24] the resolved shear stress factor (RSSF) is higher in the 〈111〉 direction than in 〈001〉. Thus, critical stresses for MT are supposed to be higher for the 〈115〉 direction as compared to 〈001〉, eventually exceeding the yield strength of the material. A similar behavior was also observed by Kireeva et al. [25], who showed the evolution of critical stresses for differently oriented single crystals in the Fe–Ni–Co–Al–Ta SMA system. This clearly provides for a rationale for the low reversibility in this condition. Nevertheless, the high ultimate stresses found are thought to indicate that the TT-1250 °C conditions can be suitable candidates for excellent functional properties at lower testing temperatures, i.e. taking into account the Clausius–Clapeyron relationship. However, a reliable conclusion is hardly possible at this point, as only limited mechanical data are available for the respective orientation.
Conclusions
The influence of cold rolling and subsequent thermal treatments on grain size and texture evolution of Fe–Ni–Co–Al–Ti SMA (without Boron addition) was studied and the following conclusions could be drawn:
(1)
The dissolution temperature of the secondary β-phase is close to 1250 °C for the present composition. Since the β-phase strongly impedes grain boundary motion during annealing, the presence of the secondary phase allows direct control of grain growth and texture.
(2)
Due to full dissolution of the β-phase upon annealing at 1300 °C, secondary recrystallization of the γ-parent phase occurs leading to significant grain growth and a major modification in texture components, i.e. a change of character from Brass type to {hkl}〈001〉.
(3)
X-ray analysis reveals adequate texture evolution already in conditions following medium deformation (reduction ratios below 92%) and annealing at 1300 °C. This clearly is a significant improvement as compared to results available in the literature stating that a thickness reduction of 98.5% is required.
(4)
Good pseudoelastic performance has been obtained in a condition being characterized by a {230}〈001〉 texture after thermal treatment at 1300 °C. This is attributed to favorable grain orientations and grain sizes spanning over the entire thickness of the samples tested, effectively avoiding detrimental grain constraints in the sample volume.
Acknowledgement
Open Access funding provided by Projekt DEAL. Financial support by Deutsche Forschungsgemeinschaft (DFG) (Project No. 405372848) is gratefully acknowledged.
Open AccessThis article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.