Tribological Property of Ni₃Al Matrix Composites with Addition of BaMoO₄

The Ni₃Al matrix composites with addition of 10, 15, and 20 wt% BaMoO₄ were fabricated by powder metallurgy technique, and the tribological behaviors were studied from room temperature to 800 °C. It was found that BaAl₂O₄ formed during the fabrication process. The Ni₃Al composites showed poor tribological property below 400 °C, with high friction coefficients (above 0.6) and wear rates (above 10⁻⁴ mm³/Nm). However, the composites exhibited excellent self-lubricating and anti-wear properties at higher temperatures, and the composite with addition of 15 wt% BaMoO₄ had the lowest wear rate (1.10 × 10⁻⁵ mm³/Nm) and friction coefficient (0.26). In addition, the results also indicated that BaAl₂O₄ for the Ni₃Al composites did not exhibit lubricating property from room temperature to 800 °C.