Tunable luminescence properties and energy transfer of single-phase Ca₄(PO₄)₂O: Dy³⁺, Eu²⁺ multi-color phosphors for warm white light

The novel Ca_4−x(PO₄)₂O: xDy³⁺ and Ca_4−x−y(PO₄)₂O: xDy³⁺, yEu²⁺ multi-color phosphors were synthesized by traditional solid-state reaction. The crystal structure, particle morphology, photoluminescence properties and energy transfer process were investigated in detail. The X-ray diffraction (XRD) results demonstrate that the products showed pure monoclinic phase of Ca₄(PO₄)₂O when x < 0.1. The scanning electron microscopy (SEM) indicated that the phosphors were grain-like morphologies with diameters of ~ 3.7–7.0 μm. Under excitation of 345 nm, Dy³⁺-doped Ca₄(PO₄)₂O phosphors showed multi-color emission bands at 410, 481 and 580 nm originated from oxygen vacancies and Dy³⁺. Interestingly, Ca₄(PO₄)₂O: Dy³⁺, Eu²⁺ phosphors exhibited blue emission band at 481 nm and broad emission band from 530 to 670 nm covering green to red regions. The energy transfer process from Dy³⁺ to Eu²⁺ was observed for the co-doped samples, and the energy transfer efficiency reached to 60% when Eu²⁺ molar concentration was 8%. In particular, warm/cool/day white light with adjustable CCT (2800–6700 K) and high CRI (R_a > 85) can be obtained by changing the Eu²⁺ co-doping contents in Ca₄(PO₄)₂O: Dy³⁺, Eu²⁺ phosphors. The optimized Ca_3.952(PO₄)₂O: 0.04Dy³⁺, 0.008Eu²⁺ phosphor can achieve the typical white light with CCT of 4735 K and CRI of 87.