Ultraviolet upconversion luminescence in Y₂O₃:Yb³⁺,Tm³⁺ nanocrystals and its application in photocatalysis

Infrared-to-ultraviolet upconversion luminescence agent Y₂O₃:Yb³⁺,Tm³⁺ was prepared by a combustion method using citrate as a fuel/reductant. The prepared sample was characterized by X-ray diffraction, SEM, and fluorescence spectrophotometer. Two unusual ¹I₆ → ³H₆ (~297 nm) and ¹D₂ → ³H₆ (~363 nm) emissions from Tm³⁺ ions were observed at room temperature under 980-nm laser excitation. The change of upconversion emission intensity depending on the Yb³⁺ concentrations was discussed. The results showed that modest Yb³⁺ doping could make the upconversion emission of Tm³⁺ intense, and high Yb³⁺ concentrations might lead to fluorescence quenching. Moreover, the influence of ultraviolet upconversion luminescence on the photodegradation of methyl orange aqueous solution under solar light irradiation in the presence of TiO₂ catalyst doped with Y₂O₃:Yb³⁺,Tm³⁺ was also investigated. It was concluded from the experiment of this study that TiO₂/Y₂O₃:Yb³⁺,Tm³⁺ composite had higher photocatalytic activity than pure TiO₂ under solar light. This study would make TiO₂ utilize sunlight more efficiently and accelerate the practical application of photocatalytic technology in water treatment region.