A Comparative Study on the Static Recrystallization Behavior of Cold-Rolled Mg-3Al-1Zn Alloy Stimulated by Electropulse Treatment and Conventional Heat Treatment

Cold-rolled AZ31 Mg alloy strips, with a reduction of 33 pct, were subjected to electropulse treatment (EPT) and conventional heat treatment (HT) to evaluate the respective influences of electropulses and temperature on the recrystallization behavior of AZ31. The highest measured temperature during the EPT (543 K) was used in HT. The electron backscattered diffraction results demonstrated that the EPT-stimulated recrystallization was completed within 8 seconds, whereas for HT, recrystallization was still far from completion even after 240 seconds. It was found that both the nucleation and grain growth of these two processes were totally different. In the EPT samples, nucleation tended to occur preferentially near extension twin boundaries and grain boundaries by continuous recrystallization, whereas in the HT samples, nucleation occurred mainly by grain boundaries bulging via discontinuous recrystallization. As grain growth proceeded, the texture intensities of the EPT samples decreased gradually and finally evolved into an obvious transverse-direction-split texture. This is likely attributable to the impact of electropulses on the boundary energy and the contribution of nonbasal dislocations; however, the basal-type textures of the HT samples were notably strengthened, which is associated with a 30 deg〈0001〉 orientation with respect to the deformed texture.