Analysis of cyclic vacuum drying curve

The objective of this research was to analyze the cyclic vacuum drying curve within one cycle. Red oak specimens of two different groups, square in cross-section, were used. Group one was comprised of four different thicknesses (2.54, 3.81, 5.08, and 6.35 cm) with a length of 25.4 cm and group two was comprised of three different lengths (12.7, 25.4, and 38.1 cm) with the thickness of 2.54 cm. The specimens were heated to 60°C in the heating oven and then dried in the vacuum oven at 18 mm Hg. The vacuum oven was at room temperature (20°C). The vacuum pump was kept running for 140 min. It was found that the cyclic vacuum drying curve consisted of two distinct parts. The fast drying period lasted about 10 to 15 min. The slow drying period occurred when the pressure inside wood approached the ambient pressure. Most of the moisture was removed during the fast drying period.