Journal of Materials Engineering and Performance
Published in: Journal of Materials Engineering and Performance 12/2020

13-11-2020

CO2 Corrosion Behavior of High-Strength and Toughness V140 Steel for Oil Country Tubular Goods

Authors: Xiuhua Gao, Dazheng Zhang, Yong Lu, Zhongtao Fan, Linxiu Du, Guo Yuan, Chunlin Qiu, Jian Kang

Published in: Journal of Materials Engineering and Performance | Issue 12/2020

Log in

Activate our intelligent search to find suitable subject content or patents.

search-config
loading …

Abstract

The CO2 corrosion behavior of V140 steel for oil country tubular goods exposed to high-temperature and pressure environment was studied by immersion corrosion experiments. The morphology, composition and elemental analysis of corrosion products were conducted by scanning electron microscope, x-ray diffractometer and electron probe micro-analyzer, respectively. The results showed that the corrosion rate gradually decreased and tended to be stable with the extension of corrosion time. The corrosion products in the initial stage were FeOOH and Fe2O3, and the final corrosion product was FeCO3. With the extension of corrosion time, corrosion products gradually became thick and dense from sparse. The fine and dense FeCO3 layer effectively improved the CO2 corrosion resistance of V140 steel.
previous article Superior Corrosion Resistance of Ti-Al-Zr Alloy in Aggressive Nitric Acid Environments
next article Microstructural and Mechanical Properties of Cu-Based Co-Mo-Reinforced Composites Produced by the Powder Metallurgy Method

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

inform now

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

inform now
Literature
1.
H. Li, Y. Zhang, and L. Han, Development Situation of OCTG and Production Localization of Hi-grade OCTG, Steel Pipe, 2008, 37(1), p 1–6
2.
Z. Liu, Y. Chen, H. Hu, and L. Niu, The Domestic and Foreign Research Status of High Strength and High Toughness of OCTG, Petrol. Tubul. Goods Instrum., 2017, 3(6), p 5–8
3.
M. Luo, M. Liu, X.T. Wang, M.C. Li, X. Li, Z.M. Ren, G.H. Cao, and Z.H. Zhang, Effect of Tempering Temperature at High Temperature Zone on Sulfide Stress Cracking Behavior for Casing Steel, Eng. Fail. Anal., 2019, 105, p 227–236CrossRef
4.
R.H. Huasler and D.E. Stenglnan, CO2 Corrosion and Its Prevention by Chemical Inhibition Oil and Gas Production, Corrosion, 1988, 44(1), p 5–9
5.
M. Lu, Z. Bai, X. Zhao, G. Zhao, J. Luo, and C. Chen, Actuality and Typical Cases for Corrosion in the Process of Extraction, Gathering, Storage and Transmission for Oil and Gas, Corros. Prot., 2003, 23(3), p 105–112
6.
Y. Li and J. Han, Research Progress and Prospect of the Application Technology of Tubing and Casings, Baosteel Technol., 2009, 6, p 27–31
7.
B. Li, M. Luo, Z. Yang, F. Yang, H. Liu, H. Tang, Z. Zhang, and J. Zhang, Microstructure Evolution of the Semi-macro Segregation Induced Banded Structure in High Strength Oil Tubes During Quenching and Tempering Treatments, Materials, 2019, 12(20), p 3310CrossRef
8.
9.
J. Wang, K. Deng, Z. Yin, B. Liu, Y. Lin, and Y. Feng, Study of Technical Specifications for Non-API, 140 Casing in Ultra-Deep Well, Eng. Fail. Anal., 2019, 97, p 115–127CrossRef
10.
H.K. Abadeh and M. Javidi, Assessment and Influence of Temperature, NaCl and H2S on CO2 Corrosion Behavior of Different Microstructures of API, 5L X52 Carbon Steel in Aqueous Environments, J. Nat. Gas Sci. Eng., 2019, 67, p 93–107CrossRef
11.
L. Wei, X. Pang, C. Liu, and K. Gao, Formation Mechanism and Protective Property of Corrosion Product Scale on X70 Steel Under Supercritical CO2 Environment, Corros. Sci., 2015, 100, p 404–420CrossRef
12.
A. Kahyarian, M. Singer, and S. Nesic, Modeling of Uniform CO2 Corrosion of Mild Steel in Gas Transportation Systems: A Review, J. Nat. Gas Sci. Eng., 2016, 29, p 530–549CrossRef
13.
Z. Liu, X. Gao, L. Du, J. Li, X. Zhou, X. Wang, Y. Wang, C. Liu, G. Xu, and R.D.K. Misra, Hydrogen Assisted Cracking and CO2 Corrosion Behaviors of Low-Alloy Steel with High Strength Used for Armor Layer of Flexible Pipe, Appl. Surf. Sci., 2018, 440, p 974–991CrossRef
14.
T.C. Almeida, M.C.E. Bandeira, R.M. Moreira, and O.R. Mattos, New Insights on the Role of CO2 in the Mechanism of Carbon Steel Corrosion, Corros. Sci., 2017, 120, p 239–250CrossRef
15.
L. Wei, K. Gao, and Q. Li, Corrosion of Low Alloy Steel Containing 0.5% Chromium in Supercritical CO2-Saturated Brine and Water-Saturated Supercritical CO2 Environments, Appl. Surf. Sci., 2018, 440, p 524–534CrossRef
16.
R. Barker, D. Burkle, T. Charpentier, H. Thompson, and A. Neville, A Review of Iron Carbonate (FeCO3) Formation in the Oil and Gas Industry, Corros. Sci., 2018, 142, p 312–341CrossRef
17.
W. Li, L. Xu, L. Qiao, and J. Li, Effect of Free Cr Content on Corrosion Behavior of 3Cr Steels in a CO2 Environment, Appl. Surf. Sci., 2017, 425, p 32–45CrossRef
18.
P.A. Alaba, S.A. Adedigba, S.F. Olupinla, O. Agboola, and S.E. Sanni, Unveiling Corrosion Behavior of Pipeline Steels in CO2-Containing Oilfield Produced Water: Towards Combating the Corrosion Curse, Crit. Rev. Solid State Mater. Sci., 2020, 45(3), p 239–260CrossRef
19.
20.
G.A. Zhang, D. Liu, Y.Z. Li, and X.P. Guo, Corrosion Behaviour of N80 Carbon Steel in Formation Water under Dynamic Supercritical CO2 Condition, Corros. Sci., 2017, 120, p 107–120CrossRef
21.
S.D. Zhu, A.Q. Fu, J. Miao, Z.F. Yin, G.S. Zhou, and J.F. Wei, Corrosion of N80 Carbon Steel in Oil Field Formation Water Containing CO2 in the Absence and Presence of Acetic Acid, Corros. Sci., 2011, 53, p 3156–3165CrossRef
22.
G.X. Zhao, X.H. Lu, J.M. Xiang, and Y. Han, Formation Characteristic of CO2 Corrosion Product Layer of P110 Steel Investigated by SEM and Electrochemical Techniques, J. Iron. Steel Res. Int., 2009, 16, p 89–94CrossRef
23.
D. Zhang, X. Gao, G. Su, Z. Liu, N. Yang, L. Du, and R.D.K. Misra, Effect of Tempered Martensite and Ferrite/Bainite on Corrosion Behavior of Low Alloy Steel Used for Flexible Pipe Exposed to High-Temperature Brine Environment, J. Mater. Eng. and Perform., 2018, 27(9), p 4911–4920CrossRef
24.
H. Antony, L. Legrand, L. Maréchal, S. Perrin, Ph Dillmann, and A. Chaussé, Study of Lepidocrocite γ-FeOOH Electrochemical Reduction in Neutral and Slightly Alkaline Solutions at 25 & #xB0;C, Electrochim. Acta, 2005, 51, p 745–753CrossRef
25.
D. de la Fuente, J. Alcántara, B. Chico, I. Díaz, J.A. Jiménez, and M. Morcillo, Characterisation of Rust Surfaces Formed on Mild Steel Exposed to Marine Atmospheres Using XRD and SEM/Micro-Raman Techniques, Corros. Sci., 2016, 110, p 253–264CrossRef
26.
M. Gao, X. Pang, and K. Gao, The Growth Mechanism of CO2 Corrosion Product Film, Corros. Sci., 2011, 53(2), p 557–568CrossRef
27.
F. Rouillard and T. Furukawa, Corrosion of 9-12Cr Ferritic-Martensitic Steels in High-Temperature CO2, Corros. Sci., 2016, 105, p 120–132CrossRef
28.
R.A. De Motte, R. Barker, D. Burkle, S.M. Vargas, and A. Neville, The Early Stages of FeCO3 Scale Formation Kinetics in CO2 Corrosion, Mater. Chem. Phys., 2018, 216, p 102–111CrossRef
29.
S. Guo, L. Xu, L. Zhang, W. Chang, and M. Lu, Characterization of Corrosion Scale Formed on 3Cr Steel in CO2-Saturated Formation Water, Corros. Sci., 2016, 110, p 123–133CrossRef
30.
T. Kamimura, S. Hara, H. Miyuki, M. Yamashita, and H. Uchida, Composition and Protective Ability of Rust Layer Formed on Weathering Steel Exposed to Various Environments, Corros. Sci., 2006, 48(9), p 2799–2812CrossRef
31.
Q.X. Li, Z.Y. Wang, W. Han, and E.H. Han, Characterization of the Rust Formed on Weathering Steel Exposed to Qinghai Salt Lake Atmosphere, Corros. Sci., 2008, 50(2), p 365–371CrossRef
32.
N. Zhang, D. Zeng, G. Xiao, J. Shang, Y. Liu, D. Long, Q. He, and A. Singh, Effect of Cl− Accumulation on Corrosion Behavior of Steels in H2S/CO2 Methyldiethanolamine (MDEA) Gas Sweetening Aqueous Solution, J. Nat. Gas Sci. Eng., 2016, 30, p 444–454CrossRef
33.
Q.Y. Liu, L.J. Mao, and S.W. Zhou, Effects of Chloride Content on CO2 Corrosion of Carbon Steel in Simulated Oil and Gas Well Environments, Corros. Sci., 2014, 84, p 165–171CrossRef
34.
Y. Hua, S. Xu, Y. Wang, W. Taleb, J. Sun, L. Zhang, R. Barker, and A. Neville, The Formation of FeCO3 and Fe3O4 on Carbon Steel and Their Protective Capabilities Against CO2 Corrosion at Elevated Temperature and Pressure, Corros. Sci., 2019, 157, p 392–405CrossRef
35.
D.Z. Zhang, X.H. Gao, L.X. Du, H.X. Wang, Z.G. Liu, N.N. Yang, and R.D.K. Misra, Corrosion Behavior of High-Strength Steel for Flexible Riser Exposed to CO2-Saturated Saline Solution and CO2-Saturated Vapor Environments, Acta Metall. Sin. Engl. Lett., 2019, 32(5), p 607–617CrossRef
36.
D.G. Li, Y.R. Feng, Z.Q. Bai, and M.S. Zheng, Characteristics of CO2 Corrosion Scale Formed on N80 Steel in Stratum Water with Saturated CO2, Appl. Surf. Sci., 2007, 253(3), p 8371–8376CrossRef
37.
L. Xu, B. Wang, J. Zhu, W. Li, and Z. Zheng, Effect of Cr Content on the Corrosion Performance of Low-Cr Alloy Steel in a CO2 Environment, Appl. Surf. Sci., 2016, 379, p 39–46CrossRef
38.
X.M. Xiao, Y. Peng, C.Y. Ma, and Z.L. Tian, Effects of Alloy Element and Microstructure on Corrosion Resistant Property of Deposited Metals of Weathering Steel, J. Iron. Steel Res. Int., 2016, 23, p 171–177CrossRef
39.
S. Jiang, F. Chai, H. Su, and C. Yang, Influence of Chromium on the Flow-Accelerated Corrosion Behavior of Low Alloy Steels in 3.5% NaCl Solution, Corros. Sci., 2017, 123, p 217–227CrossRef
40.
Y. Zhou, J. Chen, Y. Xu, and Z. Liu, Effects of Cr, Ni and Cu on the Corrosion Behavior of Low Carbon Microalloying Steel in a Cl− Containing Environment, J. Mater. Sci. Technol., 2013, 29(2), p 168–174CrossRef
Metadata
Title
CO2 Corrosion Behavior of High-Strength and Toughness V140 Steel for Oil Country Tubular Goods
Authors
Xiuhua Gao
Dazheng Zhang
Yong Lu
Zhongtao Fan
Linxiu Du
Guo Yuan
Chunlin Qiu
Jian Kang
Publication date
13-11-2020
Publisher
Springer US
Published in
Journal of Materials Engineering and Performance / Issue 12/2020
Print ISSN: 1059-9495
Electronic ISSN: 1544-1024
DOI
https://doi.org/10.1007/s11665-020-05306-7

Other articles of this Issue 12/2020

Journal of Materials Engineering and Performance 12/2020 Go to the issue

OriginalPaper

Effect of Welding Parameters on the Liquation Cracking Behavior of High-Chromium Ni-Based Superalloy

OriginalPaper

Numerical Simulation on Edge Crack of Advanced High-Strength Steel Considering Blanking Induced Damage

OriginalPaper

Investigation of Viton O-Ring Performance for the SABRE Dark Matter Experiment

OriginalPaper

Cracking of Copper Brazed Steel Joints Due to Precipitation of MnS upon Cooling

OriginalPaper

Friction Stir Welding: A Solution to Avoid Weld Cracking in Borated Stainless Steel

OriginalPaper

Hot Deformation Behavior and Dynamic Recrystallization Kinetics of a Novel Sc and Zr Modified Ultra-high-strength Al-Zn-Mg-Cu Alloy

Premium Partners

    Image Credits