Dynamic crushing characteristics of spruce wood under large deformations

An extensive series of large deformation crushing tests with spruce wood specimens was conducted. Material orientation, lateral constraint and loading rate were varied. Regarding material orientation, a reduction in the softening effect and the general force level was observed with a higher fiber-load angle. A comparison with characteristics gained by application of Hankinson’s formula showed discrepancies in compression strength and the beginning of the hardening effect. Lateral constraint of the specimens caused a multiaxial stress state in the specimens, which was quantified with the applied measuring method. Further, a higher force level compared to specimens without lateral constraint and significant hardening effect at large deformations resulted. Thus, the influence of a multiaxial stress state on the force level could be determined. An increase in the loading rate led to higher force levels at any displacement value and material orientation.