Effect of Al₂O₃ Content on Electrical Breakdown Properties of Al₂O₃/Cu Composite

Al₂O₃/Cu composites were prepared by external addition of Al₂O₃, and the effect of Al₂O₃ content on microstructure, density, hardness, electrical conductivity and vacuum electrical breakdown properties was studied. The results show that with increasing Al₂O₃ addition, the density of Al₂O₃/Cu composite significantly decreases, the hardness sharply increases and then slowly decreases, but the electrical conductivity invariably decreases. The vacuum breakdown test shows that with increasing Al₂O₃ addition, the breakdown strength first sharply increases and then decreases when the Al₂O₃ content exceeds 1.2 wt.%; the chopping current always exhibits a decreasing trend and the arc life first increases and then decreases. According to the morphology of arc erosion and analysis, the arc erosion resistance increases and then decreases sharply. In the range of experiments, the optimal arc erosion resistance of Al₂O₃/Cu composite can be obtained with the addition of 1.2 wt.% Al₂O₃.