Effect of heat treatment in air on the thermal properties of SiC fibre reinforced composite: Part 2 A magnesium aluminium silicate (MAS) matrix glass ceramic composite
Published in: Journal of Materials Science | Issue 11/2007
Log inActivate our intelligent search to find suitable subject content or patents.
Select sections of text to find matching patents with Artificial Intelligence. powered by
Select sections of text to find additional relevant content using AI-assisted search. powered by
Abstract
The thermal properties of a magnesium aluminium silicate (MAS) glass ceramic matrix composite reinforced by SiC (Nicalon) fibres have been investigated before and after heat treatment in the temperature range 600–1,200 °C. Within this temperature range, during the heat treatment at lower temperatures such as 600 and 700 °C, the oxidation of the carbon layer occurred and mixture of silicon and carbon was formed in the interface. This results in a decrease in thermal diffusivity values. After heat treatment at the temperatures higher than 1,000 °C, the carbon layer was thickened and resulted in the higher thermal diffusivity values.