Effect of heat treatment in air on the thermal properties of SiC fibre reinforced composite: Part 2 A magnesium aluminium silicate (MAS) matrix glass ceramic composite
Erschienen in: Journal of Materials Science | Ausgabe 11/2007
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
The thermal properties of a magnesium aluminium silicate (MAS) glass ceramic matrix composite reinforced by SiC (Nicalon) fibres have been investigated before and after heat treatment in the temperature range 600–1,200 °C. Within this temperature range, during the heat treatment at lower temperatures such as 600 and 700 °C, the oxidation of the carbon layer occurred and mixture of silicon and carbon was formed in the interface. This results in a decrease in thermal diffusivity values. After heat treatment at the temperatures higher than 1,000 °C, the carbon layer was thickened and resulted in the higher thermal diffusivity values.