Fabrication and characterization of La0.6Sr0.4Co0.2Fe0.8O3-δ (LSCF)-Ce0.9Gd0.1O1.95 (GDC) composite thick film for anode supported solid oxide fuel cells
Published in: Journal of Materials Science: Materials in Electronics | Issue 1/2016
Log inActivate our intelligent search to find suitable subject content or patents.
Select sections of text to find matching patents with Artificial Intelligence. powered by
Select sections of text to find additional relevant content using AI-assisted search. powered by
Abstract
Nowadays, the commercialization of solid oxide fuel cell (SOFC) is impeded by the chemical compatibility and polarization losses in association with electrode/electrolyte interface. Thus, to minimize these difficulties, the thick film of LSCF-GDC (50:50 wt%) composite was deposited onto GDC electrolyte to form perfect LSCF-GDC/GDC structure. The chemically compatibility of LSCF-GDC upon sintering of 1000 °C was confirmed from the X-ray diffraction studies. Typically, the film with 15 μm thickness possesses the porous structure, availing the free path for oxygen diffusion. The electrochemical impedance analysis of symmetric cell with LSCF-GDC as an electrode implies the relaxation of charge transfer and electrochemical reduction reaction with temperature. The NiO-GDC (30:70 wt%) supported SOFC with GDC and LSCF-GDC as an electrolyte and cathode, respectively was tested for their performance. The cell generates the maximum powder density of 315 μWcm−2 at 500 °C.