Low temperature synthesis of Co₂SiO₄/SiO₂ nanocomposite using a modified sol–gel method

The paper presents a study on the preparation of Co₂SiO₄/SiO₂ nanocomposites by a new modified sol–gel method. We have prepared gels starting from tetraethylorthosilicate (Si(OC₂H₅)₄), cobalt nitrate Co(NO₃)₂·6H₂O and some diols: ethylene glycol (C₂H₆O₂), 1,2propanediol (C₃H₈O₂) and 1,3propanediol (C₃H₈O₂), for a final composition: 30% CoO/70% SiO₂. During the heating of the gels at 140 °C, a redox reaction takes place between NO₃ ⁻ ions and diol with formation of some carboxylate anions. These carboxylate anions react with the Co(II) ions to form coordination compounds embedded in silica matrix, as evidenced by FT-IR spectrometry and thermal analysis. These Co(II) coordinative compounds thermally decompose in the range 250–300 °C to the corresponding oxides: CoO and/or Co₃O₄ inside the matrices pores. When CoO results, it reacts with SiO₂ at low temperature leading to Co₂SiO₄, which crystallizes at 700 °C. XRD patterns of the samples annealed at temperatures lower than 700 °C were characteristic to amorphous phases. The samples annealed at temperatures ≥700 °C, contain Co₂SiO₄ (olivine) as unique crystalline phase inside the amorphous silica matrix, according to XRD patterns. As evidenced by TEM images, Co₂SiO₄ nanoparticles are homogenously dispersed inside the silica matrix.