Magnetic and microwave absorption properties of W-type nanoferrite in X and Ku band
Published in: Journal of Materials Science: Materials in Electronics | Issue 3/2019
Log inActivate our intelligent search to find suitable subject content or patents.
Select sections of text to find matching patents with Artificial Intelligence. powered by
Select sections of text to find additional relevant content using AI-assisted search. powered by
Abstract
The W-type hexagonal nano ferrites (Ba0.8Al0.2Co0.9Zn1.1Fe19O27) were prepared by a modified sol–gel combustion method. The structural, morphological, magnetic and electromagnetic absorption properties were investigated, using different experimental techniques. The crystal structure, crystallite size and identification of phase were obtained from X-ray diffraction analysis. The SEM image revealed the spherical morphology of particles with nanosize dimensions. Moreover, the magnetic properties such as coercivity (Hc), saturation magnetization (Ms) and blocking temperature (TB) of prepared ferrite nanoparticles were obtained by (VSM). The hysteresis loop was measured at ± 20 kOe, which showed an increase in coercivity (Hc = 287 kOe) and decrease in saturation magnetization (MS). The reflection loss (RL) properties were measured as a function of frequency between 2 and 18 GHz. The RL curve showed 90% absorption, from 9.62 to 13.29 GHz (X-Band) and 12.8–18 GHz (Ku Band) at a coating thickness of 1 and 1.5 mm respectively.