Microstructure and Salt Fog Corrosion Behavior of AA2219 Friction-Stir-Welded Aluminum Alloy

Authors: G. Srinivasa Rao, V. V. Subba Rao, S. R. K. Rao

Published in: Metal Science and Heat Treatment | Issue 3-4/2017

Activate our intelligent search to find suitable subject content or patents.

search-config

AI-assisted search

Off

Abstract

Plates (8.1-mm-thick) from aluminum alloy AA2219-T87 are studied after friction stir welding. The plates are subjected to salt fog corrosion tests according to ASTM B117 at different pH values and different spraying times. The regions affected by corrosion are studied in different zones of welded joints by the methods of optical and transmission electron microscopy. The corrosion resistance is determined in acid, basic and neutral solutions. The resistances of the base metal and of the zones of welded joints are compared.

previous article Structure and Corrosion Resistance of Welded Joints of Alloy 1151 in Marine Atmosphere

next article A Study of the Causes of Failure of Permanent Magnets from Cast Hard Magnetic Alloys

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

inform now

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

inform now

W. M. Thomas, E. D. Nicholas, M. G. Murch, et al., “GB Patent Application No. 9125978.8, December 1991” TWI Bull., 124 (1995).

K. A. A. Hassan, P. B. Prangnell, A. F. Norman, et al., Sci. Technol. Weld. J., 8, 257 – 268 (2003), DOI: 10.1179/136217103225005480.CrossRef

J. Q. Su, T.W. Nelson, R. Mishra, and M. Mahoney, Acta Mater., 51, 713 – 729 (2003), DOI: 10.1016/S1359-6454(02)00449-4.CrossRef

C. G. Rhodes, M. W. Mahoney, W. H. Bingel, et al., Scr. Mater., 36, 69 – 75 (1997), DOI: 10.1016/S1359-6462(96)00344-2.CrossRef

K. V. Jata, K. K. Sankaran, and J. J. Ruschuu, Metall. Mater. Trans. A, 31A, 2181 – 2192 (2000), DOI: 10.1007/s11661-000-0136-9.CrossRef

G. Liu, L. E. Murr, C. S. Niou, et al., Scr. Mater. 37, 355 – 361 (1997), DOI: 10.1016/S1359-6462(97)00062-6.CrossRef

Y. S. Sato, H. Kokawa, M. Enomoto, et al., Metall. Mater. Trans. A, 30A, 3125 – 3130 (1999), DOI: 10.1007/s11661-999-0223-5.CrossRef

Y. S. Sato, H. Kokawa, M. Enomoto, and S. Jogan, Metall. Mater. Trans. A, 30A, 2429 – 2437 (1999), DOI: 10.1007/s11661-999-0251-1.CrossRef

K. V. Jata and S. L. Semiatin, Scr. Mater., 43, 743 – 749 (2000), DOI: 10.1016/S1359-6462(00)00480-2.CrossRef

10.

S. Benavides, L. E. Murr, et al., Scr. Mater., 41, 809 – 815 (1999), DOI: 10.1016/S1359-6462(99)00226-2.CrossRef

11.

M. W. Mahoney, C. G. Rhodes, J. G. Flintoff, et al., Metall. Mater. Trans. A, 29A, 1955 – 1964 (1998), DOI: 10.1007/s11661-998-0021-5.CrossRef

12.

M. Peel, A. Steuwer, M. Preuss, and P. J. Withers, Acta Mater., 51, 4791 – 4801(2005), DOI: 10.1016/S1359-6454(03)00319-7.CrossRef

13.

A. P. Reynolds, W. D. Lockwood, and T. U. Seidel, Mater. Sci. Forum, 331 – 337, 1719 – 1724 (2000).CrossRef

14.

H. J. Liu, H. Fujii, M. Maeda, and K. Nogi, J. Mater. Proc. Technol., 142, 692 – 696 (2003), DOI: 10.1016/S0924-0136(03)00660-5.CrossRef

15.

B. Yang, J. Yan, M. A. Sutton, and A. P. Reynolds, Mater. Sci. Eng. A Struct., 364, 55 – 65 (2004), DOI: 10.1016/S0921-5093(03)00532-X.CrossRef

16.

K. A. A. Hassan, A. F. Norman, and P. B. Prangnell, Mater. Sci. Forum, 396 – 402, 1549 – 1554 (2002).CrossRef

17.

K. A. A. Hassan, A. F. Norman, and P. B. Prangnell, “The effect of welding conditions on the microstructure and mechanical properties of the nugget zone in AA7010 alloy friction stir welds,” in: 3rd Int. Symp. on Friction Stir Welding, Kobe, Japan (2001).

18.

K. V. Jata, Mater. Sci. Forum, 331 – 337, 1701 – 1712 (2000).CrossRef

19.

K. A. A. Hassan, A. F. Norman, D. A. Price and P. B. Prangnell, Acta Mater., 51, 1923 – 1936 (2003), DOI: 10.1016/S1359-6454(02)00598-0.CrossRef

20.

J. D. Robson, A. Sullivan, H. R. Schercliff, and G. McShane, “Microstructural evolution during friction stir welding of AA7449,” in: 5th Int. Friction Stir Welding Symposium, Metz, France (2004).

21.

J. B. Lumsden, M. W. Mahoney, G. Pollock, and C. G. Rhodes, Corrosion, 55(12), 1127 – 1135 (1999), DOI: 10.5006/1.3283950.CrossRef

22.

Y. Li, L. E. Murr, and J. C. McClure, Mater. Sci. Eng., A271, 213 – 223 (1999), DOI: 10.1016/S0921-5093(99)00204-X.CrossRef

23.

F. Hannour, A. Davenport, and M. Srangwood, “Corrosion of friction stir welds in high strength aluminum alloys,” in: 2nd Int. Symp. on Friction Stir Welding, Gothenburg, Sweden (2000).

24.

R. Ambat, M. Jariyaboon, A. J. Davenport, et al., “Micro-electrochemical investigation of friction stir welds in aluminum aerospace alloy 2024,” in: 15th Int. Corrosion Congress, Granada, Spain (2002).

25.

J. B. Lumsden, M. W. Mahoney, C. G. Rhodes, and G. A. Pollock, Corrosion, 59, 212 – 219 (2003), DOI: 10.5006/1.3277553.CrossRef

26.

J. B. Lumsden, M. W. Mahoney, G. A. Pollock, and C. G. Rhodes, Corrosion, 55, 1127 – 1135 (1999), DOI: 10.5006/1.3283950.CrossRef

27.

C. S. Paglia, M. C. Carroll, B. C. Pitts, et al., Mater. Sci. Forum, 396 – 402, 1677 – 1684 (2002).CrossRef

28.

W. Hu and E. I. Meletis, Mater. Sci. Forum, 331 – 337, 1683 – 1688 (2000).CrossRef

29.

G. S. Frankel and Z. Xia, Corrosion, 55, 139 – 150 (1999), DOI: 10.5006/1.3283974.CrossRef

30.

J. Corral, E. A. Trillo, Y. Li, and L. E. Murr, J. Mater. Sci. Lett., 19, 2117 – 2122 (2000), DOI: 10.1023/A:1026710422951.CrossRef

31.

F. Zucchi, G. Trabanelli, and V. Grassi, Mater. Corros. 52, 853 – 859 (2001), DOI: 10.1002/1521-4176(200111)52:11 <853::AIDMACO853>3.0.CO;2-1.

32.

G. Biallas, R. Braun, C. D. Donne, et al., “Mechanical properties and corrosion behavior of friction stir welded 2024-T3,” in: 1st Int. Symp. on Friction StirWelding, Thousand Oaks, CA(1999).

33.

A. Aquillace, A. D. Fenzo, G. Giorleo, and F. Bellucci, J. Mater. Proc. Technol., 152, 97 – 105 (2004), DOI: 10.1016/j.jmatprotec.2004.03.022.CrossRef

34.

S. Williams, R. Ambat, D. Price at al., Mater. Sci. Forum, 426 – 432, 2855 – 2860 (2003).

35.

B. J. Connoly, A. J. Davenport, M. Jariyaboon, et al., “Localised corrosion friction stir welds in aluminum alloys” in: 5th Int. Friction Stir Welding Symposium, Mertz, France (2004),

36.

Standard Practice for Operating Salt Spray Apparatus, ASTM B117, American Soc. for Testing of Materials (2003).

37.

C. S. Paglia and R. C. Buchheit, Mater. Sci. Eng. A, 492, 250 (2008).CrossRef

38.

K. S. Arora, S. Pandey, M. Scharper, and R. Kumar, “Microstructure evolution during friction stir welding of aluminum alloy AA2219,” J. Mater. Sci. Technol., 26(8), 747 – 753 (2010).CrossRef

39.

K. A. A. Hassan, P. B. Prangnell, A. F. Norman, et al., Sci. Technol. Weld. Joining, 8(4), 257 – 268 (2003).CrossRef

40.

Y. Sato, H. Kokawa, M. Enomoto, and S. Jogan, “Microstructural evolution of 6063 aluminum during friction-stir welding,” Metall. Mater. Trans., A30, 24 – 29 (1999).

41.

K. Surekha, B. S. Murty, and K. Prasada Rao, “Effect of processing parameters on the corrosion behavior of friction stir processed AA2219 aluminum alloy,” Solid State Sci., 11, 907 – 917 (2009).CrossRef

Title: Microstructure and Salt Fog Corrosion Behavior of AA2219 Friction-Stir-Welded Aluminum Alloy
Authors: G. Srinivasa Rao
V. V. Subba Rao
S. R. K. Rao
Publication date: 28-07-2017
Publisher: Springer US
Published in: Metal Science and Heat Treatment / Issue 3-4/2017
Print ISSN: 0026-0673
Electronic ISSN: 1573-8973
DOI: https://doi.org/10.1007/s11041-017-0133-x

Springer Professional

Abstract

Please log in to get access to your license.

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Other articles of this Issue 3-4/2017

A Study of the Causes of Failure of Permanent Magnets from Cast Hard Magnetic Alloys

Effect of Zn and Mn Additions on the Wear Resistance of Cast Alloy Mg – 5% Al – 1% Si

Effect of Parameters of Deformation and Thermal Deformation Aging on the Impact Toughness of Structural Steel After TMT and HT

Control of the Structure of Diffusion Layer in Carbon Steels Under Nitriding with Preliminary Deposition of Copper Oxide Catalytic Films

Effect of Iron Impurity on the Phase Composition, Structure and Properties of Magnesium Alloys Containing Manganese and Aluminum

Electromechanical Surface Hardening of Tubing Steels

Premium Partners