Novel wet-chemical synthesis and characterization of nanocrystalline CeO₂ and Ce_0.8Gd_0.2O_1.9 as solid electrolyte for intermediate temperature solid oxide fuel cell (IT-SOFC) applications

Novel wet-chemical methods of synthesis have been adopted to synthesize nano-crystalline CeO₂ and Gd-substituted compositions aiming to explore an efficient oxide ion conducting solid electrolyte for intermediate temperature solid oxide fuel cell (IT-SOFC) applications. Nano-crystalline CeO₂ powders were synthesized by combustion method using redox mixture of cerric ammonium nitrate or cerium nitrate and maleic acid or 1,3-dimethylurea and compared with high surface area CeO₂ powders prepared by hydrothermal technique with microwave precipitated precursor from aqueous solutions of (NH₄)₂Ce(NO₃)₆ and urea. The grain size achieved by the hydrothermal technique is ∼7 nm which is smaller than that of commercial nano CeO₂ powders. Conventional or microwave sintering was used to prepare dense Ce_0.8Gd_0.2O_1.9 pellets from the ceria powders made of redox mixture of cerium nitrate, 1,3-dimethylurea (DMU) and Gd₂O₃ as the starting ingredients. The samples were characterized by X-ray diffractometry (XRD), transmission electron microscopy (TEM), diffuse reflectance spectroscopy (DRS), scanning electron microscopy (SEM), and ac impedance spectroscopy. The ionic conductivity measured for the pellet sintered at 1400 °C is 1 × 10⁻² and 2.4 × 10⁻² S/cm at 700 °C and 800 °C respectively.