Preparation and characterization of multiresponsive polymer composite microspheres with core–shell structure

Fe₃O₄/SiO₂/poly (N-isopropylacrylamide-co-N,N-dimethylaminoethyl methacrylate) [P(NIPAM-co-DMA)] multiresponsive composite microspheres with core–shell structure were synthesized by template precipitation polymerization. First, the magnetite nanoparticles were coated with silica and then modified with 3-(trimethoxysilyl)-propyl methacrylate (MPS). Subsequently, the Fe₃O₄/SiO₂ particles grafted with MPS were used to seed the precipitation copolymerization of NIPAM and DMA. The composite microspheres with core–shell structure were superparamagnetic, pH-sensitive, and thermoresponsive. The swelling ratio (D_{25 °C, pH = 3}/D_{50 °C, pH = 9})³ coupling of pH and temperature increased up to 21.2, which was much higher than that without comonomer DMA.