Preparation of core-shell structured hollow glass microspheres/BaFe₁₂O₁₉/Ag composites with excellent microwave absorbing properties

Hollow glass microspheres/barium ferrite (HGM/BaFe₁₂O₁₉) was first prepared via co-precipitation reaction, which was then performed to fabricate the HGM/BaFe₁₂O₁₉/Ag composites by chemical plating method. Scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), and vibrating sample magnetometry (VSM) were utilized to characterize the structures, morphologies and properties of the resultant composites. Results showed that a homogeneous and complete BaFe₁₂O₁₉ shell was coated on the surface of the HGM, and HGM/BaFe₁₂O₁₉ composites were also fully covered with Ag particles. The conductivity of the HGM/BaFe₁₂O₁₉/Ag composites was 1.24 × 10² S/cm, whereas the saturation magnetizations of the composites was reduced to 12.76 emu/g. The microwave absorption properties of the HGMs/BaFe₁₂O₁₉/Ag composites were significantly improved compared with those of HGMs/BaFe₁₂O₁₉ composites and BaFe₁₂O₁₉ particles. The reflection loss (R) showed that the bandwidth of reflection loss of HGM/BaFe₁₂O₁₉/Ag less than −10 dB (90% absorption) was 2.1 GHz (from 10.3 to 12.4 GHz), herein, the minimum loss value was −19.7 dB at 12.4 GHz.