Synthesis and photoluminescence properties of LiEu(W,Mo)₂O₈:Bi³⁺ red-emitting phosphor for white-LEDs

LiEu_1−x(W_2−yMo_y)O₈:xBi³⁺ series red-emitting phosphors were synthesized by solid state reaction. The structure, morphology, and photoluminescent properties of phosphors were studied by X-ray powder diffraction, scanning electron microscopy, and photoluminescence spectrum, respectively. X-ray powder diffraction analysis showed that the as-obtained phosphors belong to the scheelite structure. The average particle size of the investigated phosphor was about 8 μm. The excitation spectrum exhibits a charge-transfer broad band along with some sharp peaks from the typical 4f–4f transitions of Eu³⁺. Under excitation of UV, near-UV, or blue light, these phosphors showed strong red emission at 615 nm due to ⁵D₀–⁷F₂ transition of Eu³⁺. The incorporation of Mo⁶⁺ into LiEuW₂O₈:Bi³⁺ could induce red-shift of the charge-transfer broad band and a remarkable increase of photoluminescence. The highest red-emission intensity was observed with LiEu_0.80Mo₂O₈:0.20Bi³⁺. Compared with the commercial red-emitting phosphor, Y₂O₂S:Eu³⁺, the emission intensity of LiEu_0.80Mo₂O₈:0.20Bi³⁺ phosphor is much stronger than that of Y₂O₂S:Eu³⁺ and its chromaticity coordinates are closer to the standard values than that of the commercial phosphor. The optical properties of LiEu_0.80Mo₂O₈:0.20Bi³⁺ phosphor make it attractive for the application in white-light-emitting diodes (LEDs), in particular for near-UV InGaN-based white-LEDs.