The effects of oxygen concentration on ultraviolet luminescence of ZnO films by sol–gel technology and annealing

ZnO thin films were successfully deposited on SiO₂/Si substrate using the sol–gel technique and annealed in various annealing atmospheres at 900 °C by rapid thermal annealing (RTA). X-ray diffraction revealed the (002) texture of ZnO thin films. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) showed that the grains of the ZnO thin film were enlarged and its surface was smoothed upon annealing in oxygen. PL measurement revealed two ultraviolet (UV) luminescence bands at 375 and 380 nm. The intensity of the emission peak at 380 nm became stronger as the concentration of oxygen in the annealing atmosphere increased. The X-ray photoelectron spectrum (XPS) demonstrated that a more stoichiometric ZnO thin film was obtained upon annealing in oxygen and more excitons were generated from the radiative recombination carriers consistently. Additionally, the UV intensity increased with the thickness of ZnO thin film.