Thermally stable Ba0.8Ca0.2TiO3–Bi(Mg0.5Zr0.5)O3 solid solution with low dielectric loss in a broad temperature usage range
Published in: Journal of Materials Science: Materials in Electronics | Issue 6/2016
Log inActivate our intelligent search to find suitable subject content or patents.
Select sections of text to find matching patents with Artificial Intelligence. powered by
Select sections of text to find additional relevant content using AI-assisted search. powered by
Abstract
Lead-free (1−x)Ba0.8Ca0.2TiO3–xBi(Mg0.5Zr0.5)O3 [(1−x)BCT–xBMZ, 0 ≤ x ≤ 0.3] ceramics were fabricated via a conventional solid-state reaction method. The structure and dielectric properties of BCT–BMZ ceramics were systematically investigated. X-ray diffraction patterns and Raman spectra show that a systematically structural change form a tetragonal to pseudo-cubic phase occurred at about x = 0.06–0.08. As x values increased to 0.3, the temperature stability of permittivity of ceramics was markedly increased (Δε/ε
27 °C ≤ ±15 %) and low dielectric loss (≤2 %) was obtained over a wide temperature range from 27 to 290 °C at 1 kHz. These results indicate that (1−x)BCT–xBMZ ceramics are promising candidates for thermally stabile devices.