Thermodynamic Analysis of the Cu-As-S-(O) System Relevant to Sulfuric Acid Baking of Enargite at 473 K (200 °C)

While the growing demand for copper has compelled the industry to adapt new technologies for the treatment of copper-arsenic (enargite) concentrates, the refractory nature of such concentrates combined with the troublesome presence of arsenic has created a major metallurgical and environmental challenge. Preliminary results of the acid bake-leach process at the University of Utah have shown some potential advantages for the treatment of enargite concentrates. While the transformation of enargite to copper sulfate, arsenolite, and elemental sulfur has already been established experimentally, thermodynamic evaluation of the sulfuric acid baking process provides further understanding which should be useful. In this article, the available thermodynamic data for the species involved in the Cu-As-S-O system are compiled. These data were used to calculate the phase stability (Kellogg) diagrams as well as equilibrium compositions at 473 K (200 °C) using the STABCAL and HSC Chemistry^® 5.1 software packages. The equilibrium composition calculations indicate that enargite can transform to copper sulfate either directly or through chalcocite and/or covellite. The major gaseous species during baking were found to be SO₂ and H₂O. The results of the thermodynamic calculations were further compared with two confirmatory baking experiments involving a high-quality enargite sample. The condensed reaction products from sulfuric acid baking based on XRD results include CuSO₄, As₂O₃, CuO·CuSO₄, and S₈ under both neutral and oxidative conditions. While all these compounds were predicted through equilibrium calculations, some of the predicted compounds were not detected in the sulfuric acid-baked enargite. None of the calculations indicated any appreciable amounts of arsenic-bearing gases at the baking temperature of 473 K (200 °C). Consistent with thermodynamic predictions, no H₂S gas was detected during the sulfuric acid baking experiment. Approximately, 80 pct of the baked enargite samples were leached in water.