Typical Engineering Steel Defects

Authors: M. V. Maisuradze, M. A. Ryzhkov

Published in: Metallurgist | Issue 11-12/2021

Activate our intelligent search to find suitable subject content or patents.

search-config

AI-assisted search

Off

Abstract

Defects of low-carbon engineering steels 18Kh2N4MA, 25Kh2N4MA, 25G2S2N2MA reducing the operating life of components are studied. The most common metallurgical processing defects are: non-metallic inclusions, structural banding, internal cracks and pores. It is established that inclusion of titanium carbonitride significantly reduces the operating life of heavily loaded components. Defects formed during component heat and chemical heat treatment are also considered.

previous article Method for Determining the Kinematic Parameters of Longitudinal Pass Rolling

next article Opening of Sulfide Gold-Bearing Ores using Nanosecond Electromagnetic Pulses in Aqueous Medium

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

inform now

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

inform now

H. K. D. H. Bhadeshia and R. W. K. Honeycombe, Steels: Microstructure and Properties, Elsevier, UK (2017).

R. Rana and S. B. Singh, Automotive Steels. Design, Metallurgy, Processing and Applications, Elsevier, UK (2017).

V. M. Farber, O. V. Selivanova, and A. B. Arabey, “Effect of heat treatment on mechanical properties of steels of strength class K65 (X80),” Metal Science and Heat Treatment, 56, 454–456 (2014); https://doi.org/10.1007/s11041-014-9781-2.CrossRef

M. V. Maisuradze, M. A. Ryzhkov, Yu. V. Yudin, and A. A. Ershov, “Heat treatment technology for high-strength engineering steel variable cross-section components,” Metallurgist, 58, No. 7-8, 712–716 (2014); https://doi.org/10.1007/s11015-014-9982-3.

Steel and its Heat Treatment: Handbook, Swerea IVF, Molndal (2012).

M. Łomozikn, M. Zeman, and J. Brozda, “Modern martensitic steels for power industry,” Archives of Civil and Mechanical Engineering, 12, 49–59 (2012); https://doi.org/10.1016/j.acme.2012.03.010.CrossRef

Y. Luo, X. Wu, H. Wang, and Y. Min, “A comparative study on unquenched and quenched prehardened steel for large section plastic mould,” J. of Materials Processing Technology, 209, 5437–5442 (2009); https://doi.org/10.1016/j.jmatprotec.2009.04.019.CrossRef

P. Noury and K. Eriksson, “Failures of high strength stainless steel bridge roller bearings: A review,” Engineering Fracture Mechanics, 180, 315–329 (2017); https://doi.org/10.1016/j.engfracmech.2017.06.004.CrossRef

A. Lanzutti, A. Gagliardi, A. Raffaelli, M. Simonato, R. Furlanetto, M. Magnan, F. Andreatta, and L. Fedrizzi, “Failure analysis of gears, shafts and keys of centrifugal washers failed during life test,” Engineering Failure Analysis, 79, 634–641 (2017); https://doi.org/10.1016/j.engfailanal.2017.05.040.CrossRef

10.

L. P. Karpov, “Problem of unexpected failure of steel parts,” Metal Science and Heat Treatment, 40, No. 3, 122–125 (1998); https://doi.org/10.1007/BF02467473.

11.

B. M. Schönbauer, K. Yanase, and M. Endo, “Influences of small defects on torsional fatigue limit of 17–4PH stainless steel,” Int. J. of Fatigue, 100, 540–548 (2017); https://doi.org/10.1016/j.ijfatigue.2016.12.021.CrossRef

12.

W. Li, Z. Sun, Z. Zhang, H. Deng, and T. Sakai, “Influence of case-carburizing and micro-defect on competing failure behaviors of Ni–Cr–W steel under gigacycle fatigue,” Int. J. of Fatigue, 72, 66–74 (2015); https://doi.org/10.1016/j.ijfatigue.2014.11.004.CrossRef

13.

F. D’Errico, “Failures induced by abnormal banding in steels,” J. of Failure Analysis and Prevention, 10, 351–357 (2010); https://doi.org/10.1007/s11668-010-9374-3.CrossRef

14.

M. V. Maisuradze, M. A. Ryzhkov, and O. A. Surnaeva, “Effect of heat treatment on the microstructure and mechanical properties of high-strength silicon steel,”, Metallurg, No. 6, 62–66 (2016).

15.

M. V. Maisuradze and O. A. Surnayeva, “Quantitative evaluation of structural banding in structural alloy steels,” Metallurg, No. 7, 47–52 (2017).

16.

M. V. Maisuradze, M. A. Ryzhkov, A. A. Kuklina, and O. A. Surnayeva, “Effect of manufacturing technology on phase and structural transformation of silicon-containing steel,” Stal’, No. 1, 52–58 (2017).

17.

M. I. Vinograd and G. P. Gromova, Inclusions in Alloys Steels and Alloys [in Russian], Metallurgiya, Moscow (1971).

18.

Comprehensive Materials Finishing. Vol. 2. Surface and Heat Treatment Processes, Elsevier, UK (2017).

19.

G. E. Totten, L. C. F. Canale, and R. A. Mesquita, Failure Analysis of Heat Treated Steel Components, ASM International, USA (2008).

Title: Typical Engineering Steel Defects
Authors: M. V. Maisuradze
M. A. Ryzhkov
Publication date: 04-04-2021
Publisher: Springer US
Published in: Metallurgist / Issue 11-12/2021
Print ISSN: 0026-0894
Electronic ISSN: 1573-8892
DOI: https://doi.org/10.1007/s11015-021-01116-x

Springer Professional

Abstract

Please log in to get access to your license.

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Other articles of this Issue 11-12/2021

Study of the Effect of Rhenium on Heat-Resistant Titanium Alloy Mechanical Properties and Microstructure

Effect of Alloyed Coating Composition on Composite Casting Surface Layer Properties

Elevation of the Wear Resistance of Roller Dies for the Production of Wires from Titanium Alloys

Thickness Evaluation of Ceramic Coatings Formed by Microarc Oxidation

Application of a Discrete Double-Row Scraper Cleaner as an Efficient Procedure of Cleaning of Belt Conveyors Aimed at Transporting Bulk Materials

Influence of Preliminary Heat Treatment of Vanadium Sludges on the Manufacturability of their Processing

Premium Partners