Wear Behavior of the Lead-Free Tin Bronze Matrix Composite Reinforced by Carbon Nanotubes

Copper-coated carbon nanotubes were prepared by the electroless plating route. The structure and component of copper/carbon tubes were characterized using a transmission electron microscope and energy dispersive spectrometer. The results show that the surface of the carbon tubes was covered by the copper particles. Copper/carbon tubes were used as the substitute of part of tin and all of lead in the tin bronze matrix, and the tribological properties of carbon nanotube-reinforced Cu-4 wt pct Sn-6 wt pct Zn composites were studied. The effects of the carbon nanotube volume fraction and sliding distance in unlubricated ball-on-disc wear test were investigated. The 3 vol pct carbon nanotube-reinforced Cu-4 wt pct Sn-6 wt pct Zn composite shows the Vickers hardness of 126.9, which is approximately 1.6 times higher than that of Cu-6 wt pct Sn-6 wt pct Zn-3 wt pct Pb tin bronze. The wear rate and average friction coefficients of 3 vol pct carbon nanotube-reinforced Cu-4 wt pct Sn-6 wt pct Zn composite were lower than those of the Cu-6 wt pct Sn-6 wt pct Zn-3 wt pct Pb tin bronze, respectively.