Effects of rare earth Ce on properties of Sn–9Zn lead-free solder

The influences of different Ce content on the properties of Sn–9Zn lead-free solder were investigated. The results indicate that Ce plays an important role not only in the structure and the solderability, but also in the interfacial structure of Sn–9Zn–xCe/Cu and mechanical property of soldered joint. Sn–9Zn–0.08Ce shows finer and more uniform microstructure than Sn–9Zn, and when the quantity of Ce is 0.5–1 wt%, some dark Sn–Ce compounds appear in the solder. With the addition of 0.08 wt% Ce, the solderability of solder is significantly improved because the surface tension of molten solder is decreased. Adding Ce makes the Cu5Zn8 IMCs formed at the interface of solder/Cu become much thicker than that of Sn–9Zn/Cu because much more content of Zn diffuse to the interface of solder/Cu to react with Cu. Results also indicate that adding 0.08 wt% Ce to the solder enhances mechanical property of soldered joint. When the Ce content is 0.1–0.5 wt%, some hard and brittle Cu–Zn IMCs appear in the bottom of dimples and the pull force of soldered joint decreases.