Influence of coronene addition on some superconducting properties of bulk MgB₂

This study reports the effect of coronene (C₂₄H₁₂) addition on some superconducting properties such as critical temperature (T_c), critical current density (J_c), flux pinning force density (F_p), irreversibility field (H_irr), upper critical magnetic field (H_c2), and activation energy (U₀), of bulk MgB₂ superconductor by means of magnetisation and magnetoresistivity measurements. Disk-shaped polycrystalline MgB₂ samples with varying C₂₄H₁₂ contents of 0, 2, 4, 6, 8, 10 wt%, were produced at 850 °C in Ar atmosphere. The obtained results show an increase in field-J_c values at 10 and 20 K resulting from the strengthened flux pinning, and a decrease in critical temperature (T_c) because of C substitution into MgB₂ lattice, with increasing amount of C₂₄H₁₂ powder. The H_c2(0) and H_irr(0) values are respectively found as 144, 181, 172 kOe, and 128, 161, 145 kOe for pure, 4 wt% and 10 wt% C₂₄H₁₂ added samples. The U₀ depending on the magnetic field curves were plotted using thermally activated flux flow model. The maximum U₀ values are respectively obtained as 0.20, 0.23 and 0.12 eV at 30 kOe for pure, 4 wt% and 10 wt% C₂₄H₁₂ added samples. As a result, the superconducting properties of bulk MgB₂ at high fields was improved using C₂₄H₁₂, active carbon source addition, because of the presence of uniformly dispersed C particles with nanometer order of magnitude, and acting as effective pinning centres in MgB₂ structure.