Optical absorption in solution processed thin films of calcia–alumina binary compounds

UV–visible optical spectra were obtained at room temperature in air for solution-processed thin films of 12CaO·7Al₂O₃(C12A7) on the MgO <100> single crystal substrates after the post-deposition heat treatment at 1,100 °C. Two absorption peaks were observed at 5.3 and 6.1 eV and their presence was attributed to the complex electronic structure of C12A7 and its different energy levels due to the extra-framework species and the framework itself. The peak at 5.3 eV is believed to be associated with O²⁻-Cage Conduction Band type transition whereas the Framework Valence Band to Framework Conduction Band transition is responsible for the peak at 6.1 eV. The nature of electronic transition was found to be direct from the analysis due to Tauc’s law.