Optical absorption in solution processed thin films of calcia–alumina binary compounds
Erschienen in: Journal of Sol-Gel Science and Technology | Ausgabe 3/2010
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
UV–visible optical spectra were obtained at room temperature in air for solution-processed thin films of 12CaO·7Al2O3(C12A7) on the MgO <100> single crystal substrates after the post-deposition heat treatment at 1,100 °C. Two absorption peaks were observed at 5.3 and 6.1 eV and their presence was attributed to the complex electronic structure of C12A7 and its different energy levels due to the extra-framework species and the framework itself. The peak at 5.3 eV is believed to be associated with O2−-Cage Conduction Band type transition whereas the Framework Valence Band to Framework Conduction Band transition is responsible for the peak at 6.1 eV. The nature of electronic transition was found to be direct from the analysis due to Tauc’s law.