Preparation and characterization of Cu(In,Ga)Se2 thin film solar cell by printing technique with powders of quaternary alloy and NaF
Published in: Journal of Materials Science: Materials in Electronics | Issue 8/2013
Log inActivate our intelligent search to find suitable subject content or patents.
Select sections of text to find matching patents with Artificial Intelligence. powered by
Select sections of text to find additional relevant content using AI-assisted search. powered by
Abstract
This study prepared Cu(In,Ga)Se2 (CIGS) thin films on bi-layer Mo coated soda-lime glass, by printing with mixed powders of CIGS quaternary alloy (average partial size of 680 nm) and NaF. A single-stage annealing process was performed to form a CIGS chalcopyrite phase. Experimental results show stoichiometric ratios of Cu/(In+Ga) = 0.94 and Ga/(In+Ga) = 0.26 in the CIGS film. The resistivity of the sample was 12.69 Ω cm, with a carrier concentration of 9.34 × 1016 cm−3, and mobility of 5.27 cm2 V−1 s−1. The CIGS film exhibited p-type conductivity. The incorporation of 1 wt% NaF in the CIGS powder produced a chalcopyrite structure with the best crystalinity. Raman analysis identified a number of phases, including CuInSe2 and CuIn3Se5. The CIGS solar cells with AZO/i-ZnO/CdS/CIGS/Mo/soda-lime glass structure were fabricated. The CIGS thin film solar cells conversion efficiency of 1.23 % on 1 × 1.5 cm2.