Synthesis and aggregation behaviour of amphiphilic block copolymers with random middle block

The effect of microstructure on the aggregation behaviour of symmetrical di- and triblock copolymers P(BMA)-b-P(MAA) and P(BMA)-b-P(BMA-co-MAA)-b-P(MAA) with a molecular weight of 40,000 g/mol was studied. The critical micelle concentration, hydrodynamic radius and morphology of the micelles were determined by fluorescence spectroscopy, dynamic light scattering and scanning force microscopy (SFM). Whereas no effect of the microstructure on the critical micelle concentration could be detected, the hydrodynamic radius decreased from di- to triblock copolymer from 53 to 36 nm. The decrease of about 32% corresponds to the length of the random middle block within the triblock copolymer so that the reduction in hydrodynamic radius was caused by a complete orientation of the random middle block at the core corona interface. Finally, the SFM investigation showed that dehydration of micelles on a substrate is accompanied by formation of a physisorbed monolayer with a thickness of 2 nm on which the micelles are deposited.