Synthesis and microwave absorbing properties of Mn–Zn nanoferrite produced by microwave assisted ball milling

In this paper, well dispersed spinel Mn_xZn_1−xFe₂O₄ (x = 0.3,0.5 and 0.7) were obtained by microwave assisted ball milling at 2.45 GHz through only one step. The synthesized products were characterized by X-ray diffraction, high resolution transmission electron microscope, vibration sample magnetometer, and vector network analysis. Synthesized Mn–Zn nanoferrite showed the saturation magnetization reached 84.91emu/g when the x was 0.7 and the largest magnetic loss tangent at the frequency of 2.45 GHz. Microwave absorbing properties of these composites were studied at the frequency range of 2–18 GHz. Two microwave reflection loss peaks appeared for all the spinel ferrite. When x was 0.5, the minimum reflection loss appeared at the highest frequency. When x was 0.7, these two minimum reflection loss peaks, −17.36 and −48.13 dB, were calculated with the −10 dB bandwidth at the frequency ranges of 2.24–5.04 and 13.28–14.88 GHz, respectively. Resonance reflection loss peaks shifted to lower frequencies when the matching thickness increased.