Synthesis of Pr³⁺ doped or Tb³⁺–Mg codoped CaSnO₃ perovskite phosphor by the polymerized complex method

Pr³⁺ doped or Tb³⁺–Mg codoped CaSnO₃ phosphor powder with perovskite structure was synthesized by the polymerized complex method. Powder samples crystallized into the perovskite phase at approximately 600 °C, which is 400 °C lower than the crystallization temperature for the solid-state reaction method. Uniform-sized powders with average particle sizes of 1–2 μm were obtained after heat treatment at 1,400 °C. Although the samples heat-treated at 600 °C did not exhibit photoluminescence, white photoluminescence of Pr³⁺ doped CaSnO₃ or green photoluminescence of Tb³⁺–Mg codoped CaSnO₃ was observed from the sample heat-treated above 800 °C. The intensity of the photoluminescence increased with increase of the heat-treatment temperature and reached a maximum for heat treatment at 1,400 °C. The maximum photoluminescence intensity for the samples prepared by the polymerized complex method was larger than those prepared by solid-state reaction method, which is probably due to the homogeneous mixing of the doped rare earth ions.