Tempering Temperature Effect on Sliding Wear at High Temperatures in Mottled Cast Iron

Authors: O. A. Zambrano, J. J. Coronado, S. A. Rodríguez

Published in: Tribology Letters | Issue 2/2015

Activate our intelligent search to find suitable subject content or patents.

search-config

AI-assisted search

Off

Abstract

This research analyses the effect of the microstructure of mottled cast iron on tribological behaviour using a high temperature pin-on-disc test with a steel disc oxidised at 1,200 °C ASTM A36 as a counterbody. Three different microstructures were obtained for the mottled cast iron pins by quenching and tempering at 400 °C and 600 °C. The test temperature was varied from 200 to 600 °C with the aim of approximating the temperatures reached on surface work rolls under industrial conditions. The oxidation of the ASTM A36 disc at 1,200 °C was used to reproduce a counterbody (calamine) similar to that occurring in the hot roll mill steel under industrial conditions. The other tribological test parameters were held constant (normal load of 20 N and sliding speed of 0.05 m/s). The experimental results at the lowest test temperature (200 °C) show that the wear strongly depends on the microstructure and that the greatest friction coefficients are present at this condition. However, at higher test temperatures (400 and 600 °C), the wear resistance depends on the pin oxide stability. The highest wear rate occurs at a test temperature of 400 °C, and the lowest wear rate occurs at 600 °C. The explanations for these phenomena are discussed.

previous article In Situ Study of Model Organic Friction Modifiers Using Liquid Cell AFM; Saturated and Mono-unsaturated Carboxylic Acids

next article Pitted Surfaces Produced by Lactic Acid Lubrication and Their Effect on Ultra-Low Friction

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

inform now

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

inform now

Birks, N., Meier, G.H., Pettit, F.S.: Introduction to the high temperature oxidation of metals. Cambridge University Press, Cambridge (2006)CrossRef

Vergne, C., Boher, C., Gras, R., Levaillant, C.: Influence of oxides on friction in hot rolling: experimental investigations and tribological modelling. Wear 260(9–10), 957–975 (2006). doi:10.1016/j.wear.2005.06.005 CrossRef

Belzunce, F.J., Ziadi, A., Rodriguez, C.: Structural integrity of hot strip mill rolling rolls. Eng. Fail. Anal. 11(5), 789–797 (2004). doi:10.1016/j.engfailanal.2003.10.004 CrossRef

Suarez, L., Coto, R., Vanden Eynde, X., Lamberigts, M., Houbaert, Y.: High temperature oxidation of ultra-low-carbon steel. In: Öchsner, A., Grácio, J. (eds.) Defect and Diffusion Forum, pp. 158–163. Trans Tech Publications Ltd. (2007)

Pellizzari, M., Molinari, A., Straffelini, G.: Tribological behaviour of hot rolling rolls. Wear 259(7–12), 1281–1289 (2005). doi:10.1016/j.wear.2004.12.006 CrossRef

Sun, W., Tieu, A.K., Jiang, Z., Zhu, H., Lu, C.: Oxide scales growth of low-carbon steel at high temperatures. J. Mater. Process. Technol. 155–156, 1300–1306 (2004). doi:10.1016/j.jmatprotec.2004.04.172 CrossRef

Wang, S., Wei, M., Wang, F., Cui, X., Dong, C.: Transition of mild wear to severe wear in oxidative wear of H21 steel. Tribol. Lett. 32(2), 67–72 (2008)CrossRef

Wang, S.Q., Wei, M.X., Wang, F., Zhao, Y.T.: Transition of elevated-temperature wear mechanisms and the oxidative delamination wear in hot-working die steels. Tribol. Int. 43(3), 577–584 (2010). doi:10.1016/j.triboint.2009.09.006 CrossRef

Stott, F.H., Jordan, M.P.: The effects of load and substrate hardness on the development and maintenance of wear-protective layers during sliding at elevated temperatures. Wear 250(1–12), 391–400 (2001). doi:10.1016/s0043-1648(01)00601-9 CrossRef

10.

Stott, F.H.: High-temperature sliding wear of metals. Tribol. Int. 35(8), 489–495 (2002). doi:10.1016/s0301-679x(02)00041-5 CrossRef

11.

Barrau, O., Boher, C., Vergne, C., Rezai-Aria, F., Gras, R.: Investigations of friction and wear mechanisms of hot forging tool steels. Karlstad Univ 1, 81–94 (2002)

12.

Milan, J.C.G., Carvalho, M.A., Xavier, R.R., Franco, S.D., De Mello, J.D.B.: Effect of temperature, normal load and pre-oxidation on the sliding wear of multi-component ferrous alloys. Wear 259(1–6), 412–423 (2005). doi:10.1016/j.wear.2005.02.050 CrossRef

13.

Stott, F.H.: The role of oxidation in the wear of alloys. Tribol. Int. 31(1–3), 61–71 (1998). doi:10.1016/s0301-679x(98)00008-5 CrossRef

14.

Wang, L., Li, D.Y.: Effects of yttrium on microstructure, mechanical properties and high-temperature wear behavior of cast Stellite 6 alloy. Wear 255(1–6), 535–544 (2003). doi:10.1016/s0043-1648(03)00057-7 CrossRef

15.

Garza-Montes-de-Oca, N.F., Rainforth, W.M.: Wear mechanisms experienced by a work roll grade high speed steel under different environmental conditions. Wear 267(1–4), 441–448 (2009). doi:10.1016/j.wear.2009.01.048 CrossRef

16.

Pauschitz, A., Roy, M., Franek, F.: Mechanisms of sliding wear of metals and alloys at elevated temperatures. Tribol. Int. 41(7), 584–602 (2008). doi:10.1016/j.triboint.2007.10.003 CrossRef

17.

Xu, C., Gao, W.: Pilling–Bedworth ratio for oxidation of alloys. Mater. Res. Innov. 3(4), 231–235 (2000)CrossRef

18.

Chevalier, S.: Mechanisms and kinetics of oxidation. In: Cottis, B., Graham, M., Lindsay, R., Lyon, S., Richardson, T., Scantlebury, D., Stott, H. (eds.) Shreir’s Corrosion, pp. 132–152. Elsevier, Oxford (2010)CrossRef

19.

Lim, S.C.: The relevance of wear-mechanism maps to mild-oxidational wear. Tribol. Int. 35(11), 717–723 (2002). doi:10.1016/s0301-679x(02)00033-6 CrossRef

20.

Wang, S.Q., Wei, M.X., Zhao, Y.T.: Effects of the tribo-oxide and matrix on dry sliding wear characteristics and mechanisms of a cast steel. Wear 269(5–6), 424–434 (2010). doi:10.1016/j.wear.2010.04.028 CrossRef

21.

Wei, M.X., Chen, K.M., Wang, S.Q., Cui, X.H.: Analysis for wear behaviors of oxidative wear. Tribol. Lett. 42(1), 1–7 (2011). doi:10.1007/s11249-010-9741-y CrossRef

22.

Rietveld, H.M.: A profile refinement method for nuclear and magnetic structures. J. Appl. Crystallogr. 2(2), 65–71 (1969). doi:10.1107/s0021889869006558 CrossRef

23.

Larsen, A., Von Dreele, R.: GSAS: General Structure Analysis System. LANSCE, MS-H805, Los Alamos National Laboratory, Los Alamos, NM (1994)

24.

Zhou, S.X.: An integrated model for hot rolling of steel strips. J. Mater. Process. Technol. 134(3), 338–351 (2003). doi:10.1016/s0924-0136(02)01118-4 CrossRef

25.

Pellizzari, M., Cescato, D., De Flora, M.G.: Hot friction and wear behaviour of high speed steel and high chromium iron for rolls. Wear 267(1–4), 467–475 (2009). doi:10.1016/j.wear.2009.01.049 CrossRef

26.

Wang, S.Q., Yang, Z.R., Zhao, Y.T., Wei, M.X.: Sliding wear characteristics of AZ91D alloy at ambient temperatures of 25–200 °C. Tribol. Lett. 38(1), 39–45 (2010). doi:10.1007/s11249-009-9569-5 CrossRef

27.

Zhang, Q.Y., Chen, K.M., Wang, L., Cui, X.H., Wang, S.Q.: Characteristics of oxidative wear and oxidative mildwear. Tribol. Int. 61, 214–223 (2013). doi:10.1016/j.triboint.2013.01.003 CrossRef

28.

Berns, H.: Microstructure. In: Scheibelein, G. (ed.) Ferrous Materials, pp. 19–53. Springer, Berlin (2008)

29.

Jiang, J., Stott, F.H., Stack, M.M.: A mathematical model for sliding wear of metals at elevated temperatures. Wear 181–183, 20–31 (1995). doi:10.1016/0043-1648(95)90004-7 CrossRef

30.

Kennedy, F.: Frictional heating and contact temperatures. Mod. Tribol. Handb. 1, 235–272 (2001)

31.

Määttä, A., Vuoristo, P., Mäntylä, T.: Friction and adhesion of stainless steel strip against tool steels in unlubricated sliding with high contact load. Tribol. Int. 34(11), 779–786 (2001). doi:10.1016/s0301-679x(01)00074-3 CrossRef

32.

Ho-Chieh, W., Umehara, N., Kato, K.: The effect of surface roughness on friction of ceramics sliding in water. Wear 218(2), 237–243 (1998). doi:10.1016/s0043-1648(98)00208-7 CrossRef

33.

Hutchings, I.M.: Tribology: friction and wear of engineering materials. Mater. Des. 13(3), 187 (1992). doi:10.1016/0261-3069(92)90241-9 CrossRef

34.

Coronado, J.J., Gómez, A., Sinatora, A.: Tempering temperature effects on abrasive wear of mottled cast iron. Wear 267(11), 2070–2076 (2009). doi:10.1016/j.wear.2009.08.012 CrossRef

Title: Tempering Temperature Effect on Sliding Wear at High Temperatures in Mottled Cast Iron
Authors: O. A. Zambrano
J. J. Coronado
S. A. Rodríguez
Publication date: 01-02-2015
Publisher: Springer US
Published in: Tribology Letters / Issue 2/2015
Print ISSN: 1023-8883
Electronic ISSN: 1573-2711
DOI: https://doi.org/10.1007/s11249-014-0462-5

Springer Professional

Abstract

Please log in to get access to your license.

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Other articles of this Issue 2/2015

Tribological Behaviours of Wax-in-Oil Gel Deposition in Orthogonal Cleaning Process

Diffusion Equation for Spreading and Replenishment in Submonolayer Lubricant Film

Predicting Pressure–Viscosity Behavior from Ambient Viscosity and Compressibility: Challenges and Opportunities

Tribological Behavior of Sandwich-Like Self-Assembled Films Containing Silver Nanoparticles: The Influence of Outer Molecular Structure and Chain Length

In Situ Study of Model Organic Friction Modifiers Using Liquid Cell AFM; Saturated and Mono-unsaturated Carboxylic Acids

Microbubble Phenomenon in Contact Area Between Soft Tribological Interfaces in Sliding Contact

Premium Partners