TiC-Fe-Based Composite Coating Prepared by Self-Propagating High-Temperature Synthesis

TiC-Fe-based composite coatings were prepared in situ by self-propagating high-temperature synthesis combined with vacuum expendable pattern casting process. The band-like TiC phase embedded in a continuous Fe binder. There were no obvious defects and impurities at the interface between coatings and matrices. Fe presented consecutively in the coating zones and substrate zones without interruption and the microhardness in the cross-sectional area of the coating–matrix reduces continuously from the coating to the matrix area, indicating a good metallurgical bonding between the coatings and matrices. The effect of casting temperature on the microstructure and hardness of TiC-Fe-based composite coating was investigated in detail. The TiC particles formed at low casting temperature were nearly spherical in shape, and the size of TiC particles increased with increasing casting temperature due to more agglomeration. The hardness of the coatings increased first and then decreased with increasing casting temperature, and reached the highest value of 68 HRC when the casting temperature was 1773 K (1500 °C), which was twice more than that of the matrix.