Journal of Materials Engineering and Performance

Published in:

27-09-2021

The Preparation and Properties of ZnAl Coating for Ring-Shaped Bonded NdFeB Magnet with High Corrosion Resistance

Authors: Youwen Yang, Yongle Wang, Lei Yang, Ruidong Ren, Yufan Chen, Buke Dong, Jiguang Liu, Xiaogang Fang, Qinguo Gao

Published in: Journal of Materials Engineering and Performance | Issue 2/2022

Activate our intelligent search to find suitable subject content or patents.

search-config

AI-assisted search

Off

Abstract

The ZnAl coating was prepared on ring-shaped bonded NdFeB magnets (RSM) via air spraying method with silane as adhesive and flake-like Zn and Al powder as raw materials. The morphology, composition structure and element distribution of the ZnAl coating were characterized by scan electron microscopy with energy-dispersive spectroscopy and x-ray diffraction. The corrosion resistance of the ZnAl coating was analyzed by means of potentiodynamic polarization curve and neutral salt spray test (NSS). The variation in magnetic flux for RSM and ZnAl/RSM was also measured. It was found out that the Zn and Al appeared as metal elements in the coating and superimposed as sheets on the RSM and the ZnAl coating was deposited uniformly and densely with thickness of 16.7 μm. The corrosion current density of ZnAl/RSM was an order of magnitude lower than that of bare RSM and the NSS time attained to 264 h (red rust), indicating the better anticorrosion performance of the ZnAl coating. The magnetic flux of RSM was reduced by 0.15-0.55% after coated with ZnAl, indicating that the coating has little effect on the magnetic property of the RSM.

previous article Reducing Anisotropy in High Yttria Ferritic Oxide Dispersion Strengthened Steels by Powder Forging

next article Tribological Behavior of Laser Surface Melted γ-TiAl Fabricated by Electron Beam Additive Manufacturing

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

inform now

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

inform now

J.J. Croat, J.F. Herbst, R.W. Lee and F.E. Pinkerton, High-Energy Product Nd-Fe-B Permanent Magnets, Appl. Phys. Lett, 1984, 44(1), p 148–149. CrossRef

H.J. Kim, C.S. Koh and P.S. Shin, A New Anisotropic Bonded NdFeB Permanent Magnet and its Application to a Small DC Motor, IEEE Trans. Magn., 2010, 46(6), p 2314–2317. CrossRef

W.Q. Liu, R.J. Hu, M. Yue, Y.X. Yin and D.T. Zhang, Preparation and Properties of Isotropic Nd-Fe-B Bonded Magnets with Sodium Silicate Binder, J. Magn. Magn. Mater., 2017, 435, p 187–193. CrossRef

E. Maria Palmero, D. Casaleiz, N. Alejandra Jimenez, J. Rial and J. de Vicente, Magnetic-Polymer Composites for Bonding and 3D Printing of Permanent Magnets, IEEE Trans. Magn., 2019, 55(2), p 2101004.

Y.W. Song, H. Zhang, H.X. Yang and Z.L. Song, A Comparative Study on the Corrosion Behavior of NdFeB Magnets in Different Electrolyte Solutions, Mater. Corros., 2018, 59(10), p 794–801. CrossRef

L.Q. Yu, Y.H. Wen and M. Yan, Effects of Dy and Nb on the Magnetic Properties and Corrosion Resistance of Sintered NdFeB, J. Magn. Magn. Mater., 2004, 283, p 353–356. CrossRef

A.A. El-Moneim, A. Gebert, M. Uhlemann, O. Gutfleisch and L. Schultz, The Influence of Co and Ga Additions on the Corrosion Behavior of Nanocrystalline NdFeB Magnets, Corros. Sci., 2002, 44(8), p 1857–1874. CrossRef

S.C. Wang, W.P. Li, D.X. Han, H.C. Liu and L.Q. Zhu, Preparation and Application of a Waterborne Acrylic Copolymer-Siloxane Composite: Improvement on the Corrosion Resistance of Zinc-Coated NdFeB Magnets, RSC Adv., 2015, 5(99), p 81759–81767. CrossRef

W. Jiang, L. Shen, M.B. Qiu, X. Wang, M.Z. Fan and Z.J. Tian, Preparation of Ni-SiC Composite Coatings by Magnetic Field-Enhanced Jet Electrodeposition, J. Alloy. Compd., 2018, 762, p 115–124. CrossRef

10.

Y.Y. Cheng, X.L. Pang, K.W. Gao, H.S. Yang and A.A. Volinsky, Corrosion Resistance and Friction of Sintered NdFeB Coated with Ti/TiN Multilayers, Thin Solid Films, 2014, 550, p 428–434. CrossRef

11.

J.L. Xu, Z.X. Huang, J.M. Luo and Z.C. Zhong, Effect of Titania Particles on the Microstructure and Properties of the Epoxy Resin Coatings on Sintered NdFeB Permanent Magnets, J. Magn. Magn. Mater, 2014, 355, p 31–36. CrossRef

12.

K.Y. Xiao, H. Xu, Z.W. Guo and W. Zheng, Research of the Surface Treatment Process of Bonded NdFeB Magnet with Composite Powder Electrostatic Spraying, Solid State Phenom., 2018, 278, p 63–71. CrossRef

13.

P.J. Zhang, M.G. Zhu, W. Li, G.Q. Xu, X.L. Huang, X.F. Yi, J.G. Chen and Y.C. Wu, Study on Preparation and Properties of CeO₂/Epoxy Resin Composite Coating on Sintered NdFeB Magnet, J. Rare Earths, 2018, 36(5), p 544–551. CrossRef

14.

L. Jiang, Z. Jin, F. Xu, Y. Yu, G. Wei, H. Ge, Z. Zhang and C. Cao, Effect of Potential on Aluminium Early-Stage Electrodeposition Onto NdFeB Magnet, Surf. Eng., 2017, 33(5), p 375–382. CrossRef

15.

J.Z. Ma, X.F. Liu, W.T. Qu and C.G. Zhou, Corrosion Behavior of Detonation Gun Sprayed Al Coating on Sintered NFeB, J. Therm. Spray Technol., 2015, 24(3), p 394–400. CrossRef

16.

Y.Q. Huang, H.Q. Li, M. Zuo, L. Tao, W. Wang, J. Zhang, Q. Tang and P.W. Bai, Corrosion Resistance of Sintered NdFeB Coated with SiC/Al Bilayer Thin Films by Magnetron Sputtering, J. Magn. Magn. Mater., 2016, 409, p 39–44. CrossRef

17.

H. Zhang, Y.W. Song and Z.L. Song, Electrodeposited Nickel/Alumina Composite Coating on NdFeB Permanent Magnets, Mater. Corros., 2008, 59(4), p 324–328. CrossRef

18.

F. Liu, Q. Li, X.K. Yang, Y. Dai, F. Luo, S.Y. Wang and H.X. Zhang, Corrosion Resistance of Environment-Friendly Sealing Layer for Zn-Coated Sintered NdFeB Magnet, Mater. Corros., 2011, 62(12), p 1141–1148. CrossRef

19.

J.J. Ding, B.J. Xu and G.P. Ling, Al-Mn Coating Electrodeposited From Ionic Liquid on NdFeB Magnet with High Hardness and Corrosion Resistance, Appl. Surf. Sci., 2014, 305, p 309–313. CrossRef

20.

J. Chen, H. Yang, G. Xu, P. Zhang, J. Lv, W. Sun, B. Li, J. Huang, D. Wang and Y. Wu, Phosphating Passivation of Vacuum Evaporated Al/NdFeB Magnets Boosting High Anti-Corrosion Performances, Surf. Coat. Technol., 2020, 399, p 126115. CrossRef

21.

I. Rampin, F. Bisaglia and M. Dabala, Corrosion Properties of NdFeB Magnets Coated by a Ni/Cu/Ni Layer in Chloride and Sulfide Environments, J. Mater. Eng. Perform, 2010, 19(7), p 970–975. CrossRef

22.

L. Shen, Y.H. Wang, W. Jiang, X. Liu, C. Wang and Z.J. Tian, Jet Electrodeposition Multilayer Nickel on the Surface of Sintered NdFeB and Corrosion Behaviours, Corros. Eng. Sci. Technol, 2017, 52(4), p 311–316. CrossRef

23.

P.J. Zhang, J.Q. Liu, G.Q. Xu, X.F. Yi, J.G. Chen and Y.C. Wu, Anticorrosive Property of Al Coatings on Sintered NdFeB Substrates via Plasma Assisted Physical Vapor Deposition Method, Surf. Coat. Technol., 2015, 282, p 86–93. CrossRef

24.

Y.Y. Zhang, D.J. Zheng, G.L. Song, L.H. Han and D.H. Fu, Effect of Vacuum Degree on Adhesion Strength and Corrosion Resistance of Magnetron Sputtered Aluminum Coating on NdFeB Magnet, Mater. Corros., 2019, 70(7), p 1230–1241. CrossRef

25.

J.L. Li, S.D. Mao, K.F. Sun, X.M. Li and Z.L. Song, AlN/Al Dual Protective Coatings on NdFeB by DC sMagnetron Sputtering, J. Magn. Magn. Mater., 2009, 321(22), p 3799–3803. CrossRef

26.

Lasek S, Kursa M, Konecna K, Tanger L (2011) Composition, Structure and Some Corrosion Properties Of As-Recycled NdFeB Magnetic Material and Protective ZnAl Coating. In: Metal 2011 20th Anniversary international conference on metallurgy and materials, pp. 1072-1077

27.

Q.Y. Zhou, R.J. Chen and S. Guo, Preparation of Highly Corrosion-Resistant ZnAl Coating on NdFeB Magnet and Study on its Properties, Electroplat. Finish., 2020, 39, p 165–170.

28.

Y.W. Yang, R.D. Ren, Y.L. Wang, L.Z. Fang, Y.F. Chen, Q.G. Gao, L. Yang, J.G. Liu, X.G. Fang and B.K. Dong, Effect of Molding Pressure on Structure and Properties of Ring-Shaped Bonded NdFeB Magnet, IEEE Trans. Magn., 2020, 56(12), p 1000. CrossRef

29.

A.P. Yadav, H. Katayama, K. Noda, H. Masuda, A. Nishikata and T. Tsuru, Effect of Al on the Galvanic Ability of Zn-Al Coating Under Thin Layer of Electrolyte, Electrochim. Acta, 2007, 52(7), p 2411–2422. CrossRef

30.

H.Y. Gao, J. Tan, C. Ju, S.J. Chu, J. Wang and B.D. Sun, Effect of Rare Earth Metals on Microstructure and Corrosion Resistance of Zn-0.18Al Coatings, Mater. Sci. Technol., 2011, 27(1), p 71–75. CrossRef

31.

J.L. Xu, Z.C. Zhong, Z.X. Huang and J.M. Luo, Corrosion Resistance of the Titania Particles Enhanced Acrylic Resin Composite Coatings on Sintered NdFeB Permanent Magnets, J. Alloy. Compd, 2013, 570, p 28–33. CrossRef

32.

Z.Y. Cao, X.F. Ding, R. Bagheri, A.G. Wattoo, C. Xu, L.J. Yang, L.X. Song, Y.Q. Wen and L. Song, The Deposition, Microstructure and Properties of Al Protective Coatings for NdFeB Magnets by Multi-Arc Ion Plating, Vacuumb, 2017, 142, p 37–44. CrossRef

33.

J. Chen, H. Yang, G. Xu, P. Zhang, J. Lv, W. Sun, B. Li, J. Huang, D. Wang, X. Shu and Y. Wu, Rare Earth Passivation and Corrosion Resistance of Zinc Coated NdFeB Magnets, J. Rare Earths, 2020 https://doi.org/10.1016/j.jre.2020.11.012CrossRef

34.

P.J. Zhang, S.J. Deng, W. Sun, G.Q. Xu and B.S. Li, Technology and Corrosion Resistance of Electrodeposited Zn-Co Alloy Coatings on Sintered NdFeB Magnets, Metall. Funct. Mater., 2020, 27(04), p 22–29.

Title: The Preparation and Properties of ZnAl Coating for Ring-Shaped Bonded NdFeB Magnet with High Corrosion Resistance
Authors: Youwen Yang
Yongle Wang
Lei Yang
Ruidong Ren
Yufan Chen
Buke Dong
Jiguang Liu
Xiaogang Fang
Qinguo Gao
Publication date: 27-09-2021
Publisher: Springer US
Published in: Journal of Materials Engineering and Performance / Issue 2/2022
Print ISSN: 1059-9495
Electronic ISSN: 1544-1024
DOI: https://doi.org/10.1007/s11665-021-06259-1

Springer Professional

Abstract

Please log in to get access to your license.

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Other articles of this Issue 2/2022

Laser Cladding on Copper with Composite Powder C-Al2O3-Cu

Molecular Dynamics Simulation of the Tensile Deformation Behavior of the γ(TiAl)/α2(Ti3Al) Interface at Different Temperatures

Study on the Austemperability of Thin-wall Ductile Cast Iron Produced by High-Pressure Die-casting

Microstructure and Wear Properties of Electrodeposited Ni-B-Al2O3 Composite Coating on Low Carbon Steel at Elevated Temperature

Internal Damage Mechanism and Deformation Process Window of a Free-Cutting Stainless Steel Bar Rolled by Three-Roll Planetary Mill

Effect of Pre-corrosion on the Fatigue Failure of Additive Manufactured AlSi10Mg Alloy

Premium Partners