Interlaminar Shear Strength Behavior of Carbon Fiber Reinforced Aluminum Alloy Laminate

Authors: Zijing Qu, Yibo Li, Minghui Huang, Lei Dong

Published in: Mechanics of Composite Materials | Issue 5/2023

Log in

Activate our intelligent search to find suitable subject content or patents.

search-config
loading …

Abstract

The interlayer bonding ability is a crucial indicator of thermoplastic fiber metal laminates (FMLs). Using different preparation strategies and adhesive thicknesses, a series of fiber metal laminates were prepared from 2024-T3 Al alloy, unidirectional carbon fiber prepreg tapes, and films of polyether ether ketone. The span-thickness ratio for this type of laminates was examined and characterized to identify the most suitable span-thickness ratio. The effects of adhesive layer thickness on the interlaminar properties of FMLs were investigated, and the failure processes were analyzed by microscopic observation. The results show that lower span-thickness ratios have better applicability in thermoplastic carbon fiber aluminum alloy laminates. The adhesive layer presence significantly affects interlaminar properties independent of its thickness, and the FMLs with unidirectional alignment and anodized treatment possess stronger shear resistance.

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literature
1.
go back to reference M. A. Karatas and H. Gokkaya, “A review on machinability of carbon fiber reinforced polymer (CFRP) and glass fiber reinforced polymer (GFRP) composite materials,” Defence Technology, 14, No. 4, 318-326 (2018). CrossRef M. A. Karatas and H. Gokkaya, “A review on machinability of carbon fiber reinforced polymer (CFRP) and glass fiber reinforced polymer (GFRP) composite materials,” Defence Technology, 14, No. 4, 318-326 (2018). CrossRef
2.
go back to reference K. Kavitha, R. Vijayan, and T. Sathishkumar, “Fibre-metal laminates: A review of reinforcement and formability characteristics,” Materials Today: Proceedings, 22, 601-605 (2020). K. Kavitha, R. Vijayan, and T. Sathishkumar, “Fibre-metal laminates: A review of reinforcement and formability characteristics,” Materials Today: Proceedings, 22, 601-605 (2020).
3.
go back to reference T. Sinmazcelik, E. Avcu, M. O. Bora, and O. Coban, “A review: Fibre metal laminates, background, bonding types and applied test methods,” Materials & Design, 32, No. 7, 3671-3685 (2011). CrossRef T. Sinmazcelik, E. Avcu, M. O. Bora, and O. Coban, “A review: Fibre metal laminates, background, bonding types and applied test methods,” Materials & Design, 32, No. 7, 3671-3685 (2011). CrossRef
4.
go back to reference A. N. Ashong, M. Lee, S.-T. Hong, Y. S. Lee, and J. H. Kim, “Refill friction stir spot welding of dissimilar AA6014 Al alloy and carbon-fiber-reinforced polymer composite,” Metals and Mater. Int., 27, No. 4, 639-649 (2021). CrossRef A. N. Ashong, M. Lee, S.-T. Hong, Y. S. Lee, and J. H. Kim, “Refill friction stir spot welding of dissimilar AA6014 Al alloy and carbon-fiber-reinforced polymer composite,” Metals and Mater. Int., 27, No. 4, 639-649 (2021). CrossRef
5.
go back to reference A. Marx, A. Schmid, T. Haubold, L. Pursche, P. Schiebel, and A. Herrmann, “Influence of the aluminum die casting process on PEEK layered CFRP in the manufacturing of a hybrid connection,” IOP Conf. series. Mater. Sci. and Eng., 1147, No. 1, 12018 (2021). A. Marx, A. Schmid, T. Haubold, L. Pursche, P. Schiebel, and A. Herrmann, “Influence of the aluminum die casting process on PEEK layered CFRP in the manufacturing of a hybrid connection,” IOP Conf. series. Mater. Sci. and Eng., 1147, No. 1, 12018 (2021).
6.
go back to reference T. Trzepiecinski, S. M. Najm, M. Sbayti, H. Belhadjsalah, M. Szpunar, and H. G. Lemu, “New advances and future possibilities in forming technology of hybrid metal-polymer composites used in aerospace applications,” J. Compos. Sci., 5, No. 8 (2021). T. Trzepiecinski, S. M. Najm, M. Sbayti, H. Belhadjsalah, M. Szpunar, and H. G. Lemu, “New advances and future possibilities in forming technology of hybrid metal-polymer composites used in aerospace applications,” J. Compos. Sci., 5, No. 8 (2021).
7.
go back to reference Y. Lu, Y. Li, Y. Zhang, and L. Dong, “Manufacture of Al/CF/PEEK curved beams by hot stamping forming process,” Mater. and Manufac. Processes, 37, No. 14, 1597-1609 (2022). CrossRef Y. Lu, Y. Li, Y. Zhang, and L. Dong, “Manufacture of Al/CF/PEEK curved beams by hot stamping forming process,” Mater. and Manufac. Processes, 37, No. 14, 1597-1609 (2022). CrossRef
8.
go back to reference J.-H. Sim, Y. Ha, M.-K. Kim, M.-J. Kim, and Y.-R. Cho, “Investigation on delamination characteristics of 2-ply clad metals and adhesive joints for aluminum/stainless steel via the peel test,” Metals and Mater. Int., 28, No. 2, 361-369 (2022). CrossRef J.-H. Sim, Y. Ha, M.-K. Kim, M.-J. Kim, and Y.-R. Cho, “Investigation on delamination characteristics of 2-ply clad metals and adhesive joints for aluminum/stainless steel via the peel test,” Metals and Mater. Int., 28, No. 2, 361-369 (2022). CrossRef
9.
go back to reference Ostapiuk, M., M. V. Loureiro, J. Bienias and A. C. Marques, “Interlaminar shear strength study of Mg and carbon fiber-based hybrid laminates with self-healing microcapsules,” Composite Structures 255 (2021). Ostapiuk, M., M. V. Loureiro, J. Bienias and A. C. Marques, “Interlaminar shear strength study of Mg and carbon fiber-based hybrid laminates with self-healing microcapsules,” Composite Structures 255 (2021).
10.
go back to reference C. Zopp, A. Dittes, D. Nestler, I. Scharf, L. Kroll, and T. Lampke “Quasi-static and fatigue bending behavior of a continuous fiber-reinforced thermoplastic/metal laminate,” Compos., Part B, 174 (2019). C. Zopp, A. Dittes, D. Nestler, I. Scharf, L. Kroll, and T. Lampke “Quasi-static and fatigue bending behavior of a continuous fiber-reinforced thermoplastic/metal laminate,” Compos., Part B, 174 (2019).
11.
go back to reference K. Jin, S. Xuan, J. Tao, and Y. Chen, “The Synergistic effect of temperature and loading rate on deformation for thermoplastic fiber metal laminates,” Materials, 14, No. 15, 4210 (2021). K. Jin, S. Xuan, J. Tao, and Y. Chen, “The Synergistic effect of temperature and loading rate on deformation for thermoplastic fiber metal laminates,” Materials, 14, No. 15, 4210 (2021).
12.
go back to reference C. Bellini, V. Di Cocco, F. Iacoviello, and L. Sorrentino, “Performance evaluation of CFRP/Al fibre metal laminates with different structural characteristics,” Compos. Struct., 225 (2019). C. Bellini, V. Di Cocco, F. Iacoviello, and L. Sorrentino, “Performance evaluation of CFRP/Al fibre metal laminates with different structural characteristics,” Compos. Struct., 225 (2019).
13.
go back to reference T. Trzepiecinski, A. Kubit, R. Kudelski, P. Kwolek, and A. Obtloj, “Strength properties of aluminium/glass-fiberreinforced laminate with additional epoxy adhesive film interlayer,” Int. J. Adhes. and Adhes., 85, 29-36 (2018). CrossRef T. Trzepiecinski, A. Kubit, R. Kudelski, P. Kwolek, and A. Obtloj, “Strength properties of aluminium/glass-fiberreinforced laminate with additional epoxy adhesive film interlayer,” Int. J. Adhes. and Adhes., 85, 29-36 (2018). CrossRef
14.
go back to reference H. Li, Y. Hu, X. Fu, X. Zheng, H. Liu, and J. Tao, “Effect of adhesive quantity on failure behavior and mechanical properties of fiber metal laminates based on the aluminum-lithium alloy,” Compos. Struct., 152, 687-692 (2016). CrossRef H. Li, Y. Hu, X. Fu, X. Zheng, H. Liu, and J. Tao, “Effect of adhesive quantity on failure behavior and mechanical properties of fiber metal laminates based on the aluminum-lithium alloy,” Compos. Struct., 152, 687-692 (2016). CrossRef
15.
go back to reference S. Yang, W. Xu, L. Liang, T. Wang, and Y. Wei, “An experimental study on the dependence of the strength of adhesively bonded joints with thickness and mechanical properties of the adhesives,” J. Adhes. Sci. and Technol., 28, No. 11, 1055-1071 (2014). CrossRef S. Yang, W. Xu, L. Liang, T. Wang, and Y. Wei, “An experimental study on the dependence of the strength of adhesively bonded joints with thickness and mechanical properties of the adhesives,” J. Adhes. Sci. and Technol., 28, No. 11, 1055-1071 (2014). CrossRef
16.
go back to reference Q. Luo and L. Tong, “Analytical solutions for nonlinear analysis of composite single-lap adhesive joints,” Int. J. Adhes. and Adhes., 29, No. 2, 144-154 (2009). CrossRef Q. Luo and L. Tong, “Analytical solutions for nonlinear analysis of composite single-lap adhesive joints,” Int. J. Adhes. and Adhes., 29, No. 2, 144-154 (2009). CrossRef
17.
go back to reference Y. Lin, C. Liu, H. Li, K. Jin, and J. Tao, “Interlaminar failure behavior of GLARE laminates under double beam fivepoint-bending load,” Compos. Struct., 201, 79-85 (2018). CrossRef Y. Lin, C. Liu, H. Li, K. Jin, and J. Tao, “Interlaminar failure behavior of GLARE laminates under double beam fivepoint-bending load,” Compos. Struct., 201, 79-85 (2018). CrossRef
18.
go back to reference D. H. Pahr, F. G. Rammerstorfer, P. Rosenkranz, K. Humer, and H. W. Weber, “A study of short-beam-shear and doublelap-shear specimens of glass fabric/epoxy composites,” Compos., Part B, 33, No. 2, 125-132 (2002). CrossRef D. H. Pahr, F. G. Rammerstorfer, P. Rosenkranz, K. Humer, and H. W. Weber, “A study of short-beam-shear and doublelap-shear specimens of glass fabric/epoxy composites,” Compos., Part B, 33, No. 2, 125-132 (2002). CrossRef
19.
go back to reference M. Gao, P. Gao, Y. Wang, T. Lei, and C. Ouyang, “Study on metallurgically prepared copper-coated carbon fibers reinforced aluminum matrix composites,” Metals and Mater. Int., 27, No. 12, 5425-5435 (2021). CrossRef M. Gao, P. Gao, Y. Wang, T. Lei, and C. Ouyang, “Study on metallurgically prepared copper-coated carbon fibers reinforced aluminum matrix composites,” Metals and Mater. Int., 27, No. 12, 5425-5435 (2021). CrossRef
20.
go back to reference H. G. Kotik and J. E. Perez Ipina, “Short-beam shear fatigue behavior of fiber metal laminate (Glare),” Int. J. Fatigue, 95, 236-242 (2017). H. G. Kotik and J. E. Perez Ipina, “Short-beam shear fatigue behavior of fiber metal laminate (Glare),” Int. J. Fatigue, 95, 236-242 (2017).
21.
go back to reference F. Bahari-Sambran, J. Meuchelboeck, E. Kazemi-Khasragh, R. Eslami-Farsani, and S. A. Chirani, “The effect of surface modified nanoclay on the interfacial and mechanical properties of basalt fiber metal laminates,” Thin-Walled Struct., 144 (2019). F. Bahari-Sambran, J. Meuchelboeck, E. Kazemi-Khasragh, R. Eslami-Farsani, and S. A. Chirani, “The effect of surface modified nanoclay on the interfacial and mechanical properties of basalt fiber metal laminates,” Thin-Walled Struct., 144 (2019).
22.
go back to reference Y. Chen, K. Jin, H. Li, Y. Lin, Y. Lu, X. Hua, Q. Yuan, H. Wang, and J. Tao, “Effect of peer ply and cooling rate on the tensile properties of Al/Gf/PP laminate prepared by hot pressing,” J. Sandwich Struct. & Mater., 22, No 8, 2567-2581 (2020). CrossRef Y. Chen, K. Jin, H. Li, Y. Lin, Y. Lu, X. Hua, Q. Yuan, H. Wang, and J. Tao, “Effect of peer ply and cooling rate on the tensile properties of Al/Gf/PP laminate prepared by hot pressing,” J. Sandwich Struct. & Mater., 22, No 8, 2567-2581 (2020). CrossRef
23.
go back to reference R. K. Gupta, A. Mahato, and A. Bhattacharya, “Damage analysis of carbon fiber reinforced aluminum laminate under short beam and single edge notch beam bend test,” Int. J. Mech. Sci., 198, 106393 (2021). CrossRef R. K. Gupta, A. Mahato, and A. Bhattacharya, “Damage analysis of carbon fiber reinforced aluminum laminate under short beam and single edge notch beam bend test,” Int. J. Mech. Sci., 198, 106393 (2021). CrossRef
24.
go back to reference C. Liu, D. Du, H. Li, Y. Hu, Y. Xu, J. Tian, G. Tao, and J. Tao, “Interlaminar failure behavior of GLARE laminates under short-beam three-point-bending load,” Compos., Part B, 97, 361-367 (2016). CrossRef C. Liu, D. Du, H. Li, Y. Hu, Y. Xu, J. Tian, G. Tao, and J. Tao, “Interlaminar failure behavior of GLARE laminates under short-beam three-point-bending load,” Compos., Part B, 97, 361-367 (2016). CrossRef
25.
go back to reference A. C. M. Q. S. Santos, F. M. Monticeli, H. Ornaghi, Jr., L. F. d. P. Santos, and M. O. H. Cioffi, “Porosity characterization and respective influence on short-beam strength of advanced composite processed by resin transfer molding and compression molding,” Polymers & Polymer Compos., 29, No. 8, 1353-1362 (2021). A. C. M. Q. S. Santos, F. M. Monticeli, H. Ornaghi, Jr., L. F. d. P. Santos, and M. O. H. Cioffi, “Porosity characterization and respective influence on short-beam strength of advanced composite processed by resin transfer molding and compression molding,” Polymers & Polymer Compos., 29, No. 8, 1353-1362 (2021).
26.
go back to reference K. Geng, W. Yang, J. Mo, H. Liu, F. Wei, Z. Ma, Y. Zhao, and A. Inoue, “Plastic Deformation Mechanism of Ductile Fe50Ni30P13C7 Metallic Glass,” Metals and Mater. Int., 25, No. 2, 487-498 (2019). CrossRef K. Geng, W. Yang, J. Mo, H. Liu, F. Wei, Z. Ma, Y. Zhao, and A. Inoue, “Plastic Deformation Mechanism of Ductile Fe50Ni30P13C7 Metallic Glass,” Metals and Mater. Int., 25, No. 2, 487-498 (2019). CrossRef
27.
go back to reference Y. Hu, Y. Zhang, X. Fu, G. Hao, and W. Jiang, “Mechanical properties of Ti/CF/PMR polyimide fiber metal laminates with various layup configurations,” Compos. Struct., 229 (2019). Y. Hu, Y. Zhang, X. Fu, G. Hao, and W. Jiang, “Mechanical properties of Ti/CF/PMR polyimide fiber metal laminates with various layup configurations,” Compos. Struct., 229 (2019).
28.
go back to reference H. Cui, S. Koussios, Y. Li, and A. Beukers, “Measurement of adhesive shear properties by short beam shear test based on higher order beam theory,” Int. J. Adhes. and Adhes. 40, 19-30 (2013). CrossRef H. Cui, S. Koussios, Y. Li, and A. Beukers, “Measurement of adhesive shear properties by short beam shear test based on higher order beam theory,” Int. J. Adhes. and Adhes. 40, 19-30 (2013). CrossRef
29.
go back to reference J. Zhang, V. S. Chevali, H. Wang, and C.-H. Wang, “Current status of carbon fibre and carbon fibre composites recycling,” Compos., Part B, 193 (2020). J. Zhang, V. S. Chevali, H. Wang, and C.-H. Wang, “Current status of carbon fibre and carbon fibre composites recycling,” Compos., Part B, 193 (2020).
Metadata
Title
Interlaminar Shear Strength Behavior of Carbon Fiber Reinforced Aluminum Alloy Laminate
Authors
Zijing Qu
Yibo Li
Minghui Huang
Lei Dong
Publication date
31-10-2023
Publisher
Springer US
Published in
Mechanics of Composite Materials / Issue 5/2023
Print ISSN: 0191-5665
Electronic ISSN: 1573-8922
DOI
https://doi.org/10.1007/s11029-023-10141-7

Other articles of this Issue 5/2023

Mechanics of Composite Materials 5/2023 Go to the issue

Premium Partners