Erratum to: Relation between ferromagnetic layer thickness (NiCu) and properties of NiCu/Cu multilayers
Published in: Journal of Materials Science: Materials in Electronics | Issue 7/2015
Log inActivate our intelligent search to find suitable subject content or patents.
Select sections of text to find matching patents with Artificial Intelligence. powered by
Select sections of text to find additional relevant content using AI-assisted search. powered by
Excerpt
The Table 1 was incorrect in the original publication and it has been corrected in this erratum.
Table 1
Results of compositional and structural analysis of the NiCu/Cu multilayers
|
Samples
|
Compositional analysis by EDX
|
Calculated composition of NiCu layer
|
Structural analysis by XRD
|
||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
|
Ni (at. %)
|
Cu (at. %)
|
Ni (at. %)
|
Cu (at. %)
|
Texture coefficients
|
Lattice parameter a ± ∆a (nm)
|
Grain size (nm)
|
|||||
|
M111
|
M200
|
M220
|
M311
|
Experimental
|
Theoreticala
|
||||||
|
d.c plated Ni–Cu alloy
|
90
|
10
|
–
|
–
|
0.21
|
0.38
|
3.03
|
0.37
|
0.35254 ± 0.00021
|
0.35329
|
23
|
|
167[NiCu(2 nm)/Cu(1 nm)]
|
15.3
|
84.7
|
60.2
|
39.8
|
0.31
|
0.52
|
2.62
|
0.54
|
0.36031 ± 0.00069
|
0.36010
|
28
|
|
71[(NiCu(6 nm)/Cu(1 nm)]
|
59.9
|
40.1
|
85.6
|
14.4
|
0.65
|
0.56
|
2.23
|
0.39
|
0.35573 ± 0.00063
|
0.35604
|
25
|
|
56[NiCu(8 nm)/Cu(1 nm)]
|
71.4
|
28.6
|
87.6
|
12.4
|
1.00
|
0.32
|
2.21
|
0.41
|
0.35442 ± 0.00030
|
0.35499
|
27
|