A novel method for preparing lithium manganese oxide nanorods from nanorod precursor
Erschienen in: Journal of Nanoparticle Research | Ausgabe 1/2010
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
Lithium manganese oxide nanorods were prepared from manganese dioxide nanorods precursor. The structure and morphology were confirmed by X-ray diffraction (XRD) and transmission electron microscope (TEM). The data of the Rietveld refinement indicate that the nanorods preferentially grow along the [111] direction. After charge–discharge test at 1.0 mA cm−2 in 3.0–4.4 V, the nanorods LiMn2O4 showed the 134.5 mAh g−1 initial discharge capacity and only lost 1.1% of initial capacity after 30 cycles, which is better than that of bulk particles LiMn2O4 prepared by traditional solid-state reaction method. This effective and simple route to synthesis nanorods LiMn2O4 from one-dimensional (1D) precursor could also be extended to prepare 1D other nanomaterials with special electrochemical properties.