Cathodoluminescence properties of SiO₂:Pr³⁺and ZnO·SiO₂:Pr³⁺ phosphor nanopowders

The successful incorporation of ZnO nanoparticles in Pr³⁺-doped SiO₂ using a sol–gel process is reported. SiO₂:Pr³⁺ gels, with or without ZnO nanoparticles, were dried at room temperature and annealed at 600 °C. On the basis of the X-ray Diffraction (XRD) results, the SiO₂ was amorphous regardless of the incorporation of Pr³⁺ and nanocrystalline ZnO or annealing at 600 °C. The particles were mostly spherical and agglomerated as confirmed by Field Emission Scanning Electron Microscopy. Thermogravimetric analysis of dried gels performed in an N₂ atmosphere indicated that stable phases were formed at ≥900 °C. Absorption bands ascribed to ³H₄-³P_{(J = 0,1,2)}, ¹I₆ and ¹D₂ in the UV–VIS region were observed from SiO₂:Pr³⁺ colloids. The red cathodoluminescent (CL) emission corresponding to the ³P₀ → ³H₆ transition of Pr³⁺ was observed at 614 nm from dried and annealed SiO₂:Pr³⁺ powder samples. This emission was increased considerably when ZnO nanoparticles were incorporated. The CL intensity was measured at an accelerating voltage of 1-5 keV and a fixed beam current of 8.5 μA. The effects of accelerating voltage on the CL intensity and the CL degradation of SiO₂:Pr³⁺ and ZnO·SiO₂:Pr³⁺ were also investigated using Auger electron spectroscopy coupled with an Ocean Optics S2000 spectrometer.