Compressive creep behavior in air of a slightly porous as-sintered polycrystalline α-alumina material
Erschienen in: Journal of Materials Science | Ausgabe 8/2007
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
Compressive creep tests in air have been performed on a polycrystalline submicron as sintered and slightly porous α-alumina material. Two different deformation mechanisms, depending on the applied stress and creep temperature, have been identified when the grain size becomes higher than a critical value 〈G
*〉.
For low temperatures and/or low applied stresses, deformation occurs by grain boundary sliding accommodated by an in-series “interface reaction/diffusion of Al3+ cations” process, with the limiting step being the interface reaction. In this case increased densification of the samples is observed after creep, compared to the as-sintered ones.
In contrast, for high temperatures and/or high-applied stresses, deformation occurs by grain boundary sliding accommodated by the relocation and growth of preexisting cavities, the growth step being also controlled by the diffusion of Al3+ cations. In this case, a marked decrease of the relative density is measured on the crept samples compared to the as-sintered ones.
Using these results, it is possible to identify the optimal conditions for superplastic forming of previously as-sintered parts, leading to shaped objects with an increased final density.