Corrosion and Potentiostatic Polarization of an Al-Cu-Li Alloy under Tensile Stress

The stress corrosion cracking (SCC) of an Al-3.8Cu-1.5Li-0.5Zn-0.5Mg-0.3Mn alloy in 3.5% NaCl solution was studied through using slow strain rate tension(SSRT). The potentiodynamic polarization and anodic potentiostastic polarization of the stressed and stress free alloy with T6 temper were investigated. The tensile stress decreased the break down potential. The alloy was sensitive to intergranular SCC (IGSCC), due to the continuous distribution of anodic phase of T₂(Al₆CuLi₃) along the grain boundary. During the potentiostastic polarization, the current-time curve of the stressed alloy displayed a repeated transient feature that the current increased suddenly followed by a slower recovery, and corrosion crack appeared along the grain boundary. While the stress free alloy did not show this current feature and corrosion crack along the grain boundary. The repeated current transient was associated with the crack tip propagation and crack wall passivation. This feature may be used to analyze the SCC process.