Effect of Extrusion Ratio on Microstructure and Resulting Mechanical Properties of Mg Alloys with LPSO Phase

verfasst von : Klaudia Horváth, Daria Drozdenko, Gerardo Garcés, Kristián Máthis, Patrik Dobroň

Erschienen in: Magnesium Technology 2017

Verlag: Springer International Publishing

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

The WZ21 (Mg + 1.8 wt% Y + 0.7 wt% Zn) magnesium alloy having an addition of 0.5 wt% of CaO was extruded with different extrusion ratios (4:1, 10:1, 18:1) at 350 °C. In all alloys, a long-period stacking-ordered (LPSO) phase composed of Zn and Y is formed. The microstructure was analyzed by electron backscatter diffraction (EBSD) mapping. The WZ21 alloy after extrusion with the extrusion ratio of 4:1 contains large grains. The fraction of recrystallized grains increases with increasing extrusion ratio. All samples have basal planes oriented parallel to the extrusion direction (ED) and this texture weaken with increasing extrusion ratio. Mechanical properties of the samples were investigated during compression along ED at room temperature and at a constant strain rate of 10⁻³ s⁻¹. Concurrently, with the deformation tests, the acoustic emission (AE) response of the specimens was recorded. The maximum of the AE count rate in all cases corresponds to the macroscopic yield point.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Vorheriges Kapitel Development of Ultra-High Strength and Ductile Mg–Gd–Y–Zn–Zr Alloys by Extrusion with Forced Air Cooling

Nächstes Kapitel Mechanically Alloyed Magnesium Based Nanostructured Alloy Powders for Biomedical Applications

M.M. Avedesian, H. Baker: Magnesium and Magnesium Alloys (ASM Specialty Handbook). ASM International (1999) (ISBN 0-87170-657-1)

E. Abe, Y. Kawamura, K. Hayashi, A. Inoue, Long-period ordered structure in a high-strength nanocrystalline Mg-1 at% Zn-2 at% Y alloy studied by atomic-resolution Z-contrast STEM. Acta Mater. 50, 3845–3857 (2002)CrossRef

D. Egusa, E. Abe, The structure of long period stacking/order Mg–Zn–RE phases with extended non-stoichiometry ranges. Acta Mater. 60, 166–178 (2012)CrossRef

Y. Kawamura, M. Yamasaki, Formation and mechanical properties of Mg97Zn(1)Re(2) alloys with long-period stacking ordered structure. Mater. Trans. 48, 2986–2992 (2007)CrossRef

M. Yamasaki, K. Hashimoto, K. Hagihara, Y. Kawamura, Effect of multimodal microstructure on mechanical properties of Mg-Zn-Y extruded alloy. Acta Mater. 59, 3646–3658 (2011)CrossRef

Y. Kawamura, T. Kasahara, S. Izumi, M. Yamasaki, Elevated temperature Mg₉₇Z₂Cu₁ alloy with long period ordered structure. Scr. Mater 55, 453–456 (2006)CrossRef

K. Hagihara, N. Yokotami, Y. Umakoshi, Plastic deformation of Mg₁₂YZn with 18R long-period stacking ordered structure. Intermetallics 18, 267–276 (2010)CrossRef

K. Hagihara, Y. Sugino, Y. Fukusumi, Y. Umakoshi, T. Nakano, Plastuc deformation behavior of Mg₁₂ZnY LPSO-phase with 14H-typed structure. Mater. Trans. 52, 1096–1103 (2011)CrossRef

J.K. Kim, S. Sandlöbes, D. Raabe, On the room temperature deformation mechanisms of a Mg-Y-Zn alloy with long-period-stacking-ordered structures. Acta Mater. 82, 414–423 (2015)CrossRef

10.

G. Garcés, D.G. Morris, M.A. Muňoz-Morris, P. Perez, D. Tolnai, C. Mendis, A. Stark, H.K. Lim, S. Kim, N. Shell, P. Adva, Plasticity analysis by synchrotron radiation in a Mg97Y2Zn1 alloy with bimodal grain structure and containing LPSO phase. Acta Mater. 94, 78–86 (2015)CrossRef

11.

X.P. Yhang, S. Castagne, X.F. Luo, C.F. Gu, Effects of extrusion ratio on the ratcheting behavior of extruded AZ31B magnesium alloy under asymmetrical uniaxial cyclic loading. Mat. Sci. Eng. A 528, 838–845 (2011)CrossRef

12.

X. Zhang, G. Yuan, J. Niu, P. Fu, W. Ding, Microstructure, mechanical properties, biocorrosion behavior and cytotoxicity of as/extruded Mg-Nd-Yn-Yr alloy with different extrusion ratios. J. Mech. Behav. Biomed 9, 153–162 (2012)CrossRef

13.

J. Bohlen, S.B. Yi, D. Letzig, K.U. Kainer, Effect of rare earths elements on the microstructure and texture development in magnesium-manganese alloys during extrusion. Mater. Sci. Eng. A 527, 7092–7098 (2010)CrossRef

14.

P. Dobroň, F. Chmelík, S. Yi, K. Parfenenko, D. Letzig, J. Bohlen, Grain size effects on deformation twinning in an extruded magnesium alloy tested in compression. Scr. Mater. 65, 424–427 (2011)CrossRef

15.

P. Dobroň, F. Chmelík, K. Parfenenko, D. Letzig, J. Bohlen, On the Effect of the Extrusion Speed on Microstructure and Plastic Deformation of ZE10 and ZEK100 Magnesium Alloys - an Acoustic Emission Study. Acta Phys. Pol. A 122(3), 593–596 (2012)CrossRef

16.

J. Čapek, K. Máthis, B. Clausen, J. Stráská, P. Beran, P. Lukáš, Study of the loading mode dependence of the twinning in random textured cast magnesium by acoustic emission and neutron diffraction methods. Mater. Sci. Eng. A 602, 25–32 (2014)CrossRef

17.

A. Vinogradov, D. Orlov, A. Danyuk, Y. Estrin, Effect of grain size on the mechanisms of plastic deformation in wrought Mg-Zn-Zr alloy revealed by acoustic emission technique. Acta Mater. 61, 20144–22056 (2013)

18.

D.L. Yin, J.T. Wang, J.Q. Liu, X. Zhao, On tension–compression yield asymmetry in an extruded Mg–3Al–1Zn alloy. J. Alloys Compd. 478, 789–795 (2009)CrossRef

19.

W.F. Hosford, The Mechanics of Crystals and Textured Polycrystals (Oxford University Press, Oxford, 1993)

20.

C.R. Heiple, S.H. Carpenter, Acoustic emission produced by deformation of metals and alloys—a review: Part I. J. Acoust. Emission 6, 177 (1987)

21.

G. Garcés, P. Perez, S. Cabeza, H.K. Lin, S. Kim, W. Gan, P. Adeva, Reverse tension/compression asymmetry of a Mg-Y-Zn alloys containing LPSO phase. Mat. Sci. Eng. A 647, 287–293 (2015)CrossRef

22.

J. Bohlen, F. Chmelík, P. Dobroň, D. Letzig, P. Lukáč, K.U. Kainer, Acoustic emission during tensile testing of magnesium AZ alloys. J. Alloys Comp. 378, 214–219 (2004)CrossRef

Titel: Effect of Extrusion Ratio on Microstructure and Resulting Mechanical Properties of Mg Alloys with LPSO Phase
verfasst von: Klaudia Horváth
Daria Drozdenko
Gerardo Garcés
Kristián Máthis
Patrik Dobroň
Verlag: Springer International Publishing
Buch: Magnesium Technology 2017
Print ISBN: 978-3-319-52391-0

Electronic ISBN: 978-3-319-52392-7

Copyright-Jahr: 2017
DOI: https://doi.org/10.1007/978-3-319-52392-7_8

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht