Effect of HNO₃ on crystalline phase evolution in lithium silicate powders prepared by sol–gel processes

An interesting observation is reported on the dramatic effect of HNO₃ on crystalline phase evolution in the 33.3 mol% Li₂O–SiO₂ glass–ceramic (stoichiometric composition of lithium disilicate Li₂Si₂O₅, LS₂) prepared by sol–gel processes from tetraethylorthosilicate (TEOS) and lithium ethoxide precursors. Nitric acid (65%), in molar ratio HNO₃/TEOS = 0.1, was added either to the precursor sol or to 95 °C dried gel. The product, which is amorphous at temperatures below 450 °C, transforms into crystalline lithium metasilicate (Li₂SiO₃, LS) at around 550 °C (starting temperature ∼450 °C), instead of forming crystalline LS₂. Phase separation in the glassy phase may be responsible for the formation of lithium metasilicate. XRD, ²⁹Si MAS, and ⁷Li static NMR were used to follow the crystallization evolution and network structures of the materials heat-treated at various temperatures.