Effect of the introduction of vanadium pentaoxide in phospho-tellurite glasses containing gadolinium ions

A range of phospho-tellurite glasses containing gadolinium was prepared and infrared absorption spectra were measured. Structural changes, as recognized by analyzing band shapes of IR spectra, revealed that Gd₂O₃ causes a higher extent of network polymerization as far as x ≤ 15 mol% because the conversion of [TeO₄] to [TeO₃] structural units is supported by the increase of metaphosphate structural groups. While for x between 20 and 30 mol% Gd₂O₃ show some drastic structural modifications which lead to the increase in the glass fragility. Thus the addition of V₂O₅ resulted in gradual depolymerization of the phosphate chains and formation of short phosphate units, which are linked to vanadium through P–O–V bonds. The formation of P–O–V bonds increases the cross-link between the phosphate chains and the bending mode of Te–O–Te or O–Te–O linkages.