Effects of Internal Oxidation Methods on Microstructures and Properties of Al2O3 Dispersion-Strengthened Copper Alloys

verfasst von : Feng Chen, Zhiqiao Yan, Tao Wang

Erschienen in: High Performance Structural Materials

Verlag: Springer Singapore

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

With Cu–Al alloy powder as raw material and Cu2O powder as oxidant, two internal oxidation methods, namely step-by-step internal oxidation-reduction method (referred to as the step-by-step method) and integrated internal oxidation-reduction method (referred to as the integrated method), were respectively adopted to achieve the oxidation of Al. Then hot extrusion without canning was applied to prepare Al2O3 dispersion-strengthened copper alloys. The effects of the two internal oxidation methods on microstructures and properties of the alloys were compared. The results show that both the step-by-step method and the integrated method can achieve the complete oxidation of Al. However, the excessive oxidant can not be reduced thoroughly in the integrated method. The residual oxidant increases oxidation of the sintered body during hot extrusion and the formed copper oxides distribute in the grains as well as at the grain boundaries. While in the step-by-step alloy, the copper oxides mainly distribute at the grain boundaries. The step-by-step method improves electrical conductivity and ductility, but lowers hardness and strength. The integrated alloy has worse ductility and lower electrical conductivity, but strength and hardness are higher. The step-by-step alloy has better comprehensive properties, and its electrical conductivity, hardness, tensile strength, yield strength and elongation is 89% IACS, HRB 69–72, 425 MPa, 394 MPa and 27.2%, respectively.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat R.F. Need, D.J. Alexander, R.D. Field, V. Livescu, P. Papin, C.A. Swenson and D.B. Mutnick, The effects of equal channel angular extrusion on the mechanical and electrical properties of alumina dispersion-strengthened copper alloys, Mater. Sci. Eng. A 565 (2013) 450–458. R.F. Need, D.J. Alexander, R.D. Field, V. Livescu, P. Papin, C.A. Swenson and D.B. Mutnick, The effects of equal channel angular extrusion on the mechanical and electrical properties of alumina dispersion-strengthened copper alloys, Mater. Sci. Eng. A 565 (2013) 450–458.
2.
Zurück zum Zitat V. Rajkovic, D. Bozic, A. Devecerski and M.T. Jovanovic, Characteristic of copper matrix simultaneously reinforced with nano- and micro-sized Al2O3 particles, Mater. Charact. 67 (2012) 129–137. V. Rajkovic, D. Bozic, A. Devecerski and M.T. Jovanovic, Characteristic of copper matrix simultaneously reinforced with nano- and micro-sized Al2O3 particles, Mater. Charact. 67 (2012) 129–137.
3.
Zurück zum Zitat S.J. Hwang and J. Lee, Mechanochemical synthesis of Cu-Al2O3 nanocomposites, Mater. Sci. Eng. A 405 (2005) 140–146. S.J. Hwang and J. Lee, Mechanochemical synthesis of Cu-Al2O3 nanocomposites, Mater. Sci. Eng. A 405 (2005) 140–146.
4.
Zurück zum Zitat J. Lee, Y.C. Kim, S. Lee, J.K. Nack, S. Ahn and N.J. Kim, Correlation of the microstructure and mechanical properties of oxide-dispersion-strengthened coppers fabricated by internal oxidation, Metall. Mater. Trans. A 35 (2004) 493–502. J. Lee, Y.C. Kim, S. Lee, J.K. Nack, S. Ahn and N.J. Kim, Correlation of the microstructure and mechanical properties of oxide-dispersion-strengthened coppers fabricated by internal oxidation, Metall. Mater. Trans. A 35 (2004) 493–502.
5.
Zurück zum Zitat K. Dash, B.C. Ray and D. Chaira, Synthesis and characterization of copper-alumina metal matrix composite by conventional and spark plasma sintering, J. Alloy Compd. 516 (2014) 78–84. K. Dash, B.C. Ray and D. Chaira, Synthesis and characterization of copper-alumina metal matrix composite by conventional and spark plasma sintering, J. Alloy Compd. 516 (2014) 78–84.
6.
Zurück zum Zitat Z.Q. Yan, F. Chen and Y.X. Cai, Al2O3 dispersion strengthened copper alloy prepared by high-velocity compaction, Chin. J. Nonferrous Met. 25 (2015) 747–753. Z.Q. Yan, F. Chen and Y.X. Cai, Al2O3 dispersion strengthened copper alloy prepared by high-velocity compaction, Chin. J. Nonferrous Met. 25 (2015) 747–753.
7.
Zurück zum Zitat Z.Q. Yan, F. Chen, F.X. Ye, D.P. Zhang and Y.X. Cai, Microstructures and properties of Al2O3 dispersion-strengthened copper alloys prepared through different methods, Int. J. Miner. Metall. Mater. 23 (2016) 1437–1443. Z.Q. Yan, F. Chen, F.X. Ye, D.P. Zhang and Y.X. Cai, Microstructures and properties of Al2O3 dispersion-strengthened copper alloys prepared through different methods, Int. J. Miner. Metall. Mater. 23 (2016) 1437–1443.
8.
Zurück zum Zitat M.X. Guo, M.P. Wang, K. Shen, L.F. Cao, R.S. Lei and S.M. Li, Effect of cold rolling on properties and microstructures of dispersion strengthened copper alloys, Trans. Nonferrous Met. Soc. China 18 (2008) 333–339. M.X. Guo, M.P. Wang, K. Shen, L.F. Cao, R.S. Lei and S.M. Li, Effect of cold rolling on properties and microstructures of dispersion strengthened copper alloys, Trans. Nonferrous Met. Soc. China 18 (2008) 333–339.
9.
Zurück zum Zitat F. Chen, Z.Q. Yan and Y.X. Cai, Properties of Al2O3 dispersion strengthened copper alloy prepared by internal oxidation and high-velocity compaction, J. Funct. Mater. 46 (2018) 8133–8137. F. Chen, Z.Q. Yan and Y.X. Cai, Properties of Al2O3 dispersion strengthened copper alloy prepared by internal oxidation and high-velocity compaction, J. Funct. Mater. 46 (2018) 8133–8137.
10.
Zurück zum Zitat D. Feng, C.X. Shi and Z.G. Liu, Introduction to materials science, Chemical Industry Press, Beijing, 2002. D. Feng, C.X. Shi and Z.G. Liu, Introduction to materials science, Chemical Industry Press, Beijing, 2002.
11.
Zurück zum Zitat T.S. Srivatsan, N. Narendra and J.D. Troxell, Tensile deformation and fracture behavior of an oxide dispersion strengthened copper alloy, Mater. Des. 21(2000) 191–198. T.S. Srivatsan, N. Narendra and J.D. Troxell, Tensile deformation and fracture behavior of an oxide dispersion strengthened copper alloy, Mater. Des. 21(2000) 191–198.
12.
Zurück zum Zitat A. Hajri, A. Melendez, R. Woods and T.S. rivatsan, Influence of heat treatment on tensile response of an oxide dispersion strengthened copper, J. Alloy. Compd. 290 (1999) 290–297. A. Hajri, A. Melendez, R. Woods and T.S. rivatsan, Influence of heat treatment on tensile response of an oxide dispersion strengthened copper, J. Alloy. Compd. 290 (1999) 290–297.
Metadaten
Titel
Effects of Internal Oxidation Methods on Microstructures and Properties of Al2O3 Dispersion-Strengthened Copper Alloys
verfasst von
Feng Chen
Zhiqiao Yan
Tao Wang
Copyright-Jahr
2018
Verlag
Springer Singapore
DOI
https://doi.org/10.1007/978-981-13-0104-9_1

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.