Friction Analysis in Bulk Metal Forming

verfasst von : Laurent Dubar, André Dubois, Mirentxu Dubar

Erschienen in: 60 Excellent Inventions in Metal Forming

Verlag: Springer Berlin Heidelberg

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

A methodology to characterize friction according to the severe conditions of contact encountered in metal forming is presented. The main peculiarity of the proposed method is to use specimens and contactor made of industrial tool and workpiece surface in laboratory bench tests in order to ensure their representativeness regarding to the real process. Four steps are then required to identify friction: measurement/computation of mechanical loading on the process to be simulated in the lab (sliding velocities, contact pressures, plastic strains…), machining of specimens and contactors, adjustment of the friction test to simulate the target loading, analyzes of the results in terms of friction and lubricant efficiency. Examples are presented to exhibit the reliability and flexibility of the methodology.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Vorheriges Kapitel Sheet Material Characterization with the In-Plane Torsion Test: Cyclic Loading, Grooved Specimen and Twin Bridge Specimen

Nächstes Kapitel Flow Stress Measurement in Upsetting Test with Grooved Platens

P Groche, C Müller, J Stahlmann, S Zang, Mechanical conditions in bulk metal forming tribometers – Part one, Tribology International, Volume 62, 2013, Pages 223–231CrossRef

L Dubar, A Dubois, M Dubar, Friction and wear phenomena in cold metal forming: an integrated approach, Proceedings of the Institution of Mechanical Engineers, Part B: Journal of Engineering Manufacture, volume 220, 2006, pp 1–10CrossRef

A Dubois, M Dubar, L Dubar, Warm and Hot Upsetting Sliding Test: Tribology of Metal Processes at High Temperature, Procedia Engineering, Volume 81, 2014, 1964–1969CrossRef

A Dubois, E Luc, M Dubar, L Dubar, C Thibaut, JM Damasse, Initiation of Sticking during Hot Rolling of Stainless Steel Plate, Procedia Engineering 81, 2014, 1958–1963CrossRef

A Dubois, L Lazzarotto, L Dubar, J Oudin, A multi-step lubricant evaluation strategy for wire drawing–extrusion–cold heading sequence, Wear 249 (10), 951–961

M Dubar, S Huart, R Deltombe, A Dubois, L Dubar, Cold rolling of galvanized strips: A new approach to the evaluation of zinc fines formation, Journal of materials processing technology 177 (1), 2006, 505–508 CrossRef

A Belotserkovets, A Dubois, M Dubar, L Dubar, R Deltombe, H Vandekinderen, JM Damasse, 2D asperity deformation of stainless steel strip in cold rolling, International Journal of Material Forming, volume 1, 2008, 351–354CrossRef

L Dubar, C Hubert, P Christiansen, N Bay, A Dubois, Analysis of fluid lubrication mechanisms in metal forming at mesoscopic scale, CIRP Annals-Manufacturing Technology 61 (1), 2012, 271–274CrossRef

L Dubar, B Hauw, A Dubois, J Oudin, Numerical identification of coating bulk behaviour in metal forming, Computers & Structures, volume 79, 2001, 1027–1037CrossRef

10.

A Verleene, L Dubar, A Dubois, M Dubar, J Oudin, Hardening behaviour law versus rigid perfectly plastic law: application to a cold forging tool steel, International Journal of Plasticity, volume 8, 2002, 997–1011CrossRef

11.

L Lazzarotto, A Dubois, L Dubar, A Verleene, J Oudin, Testing of zinc phosphate/stearate coating according to true conditions of contact in wire drawing, Surface engineering, Volume 14, 1998, 335–338CrossRef

12.

M Dubar, A Dubois, L Dubar, Wear analysis of tools in cold forging: PVD versus CVD TiN coatings, Wear 259 (7), 2005, 1109–1116CrossRef

13.

E Daouben, A Dubois, M Dubar, L Dubar, R Deltombe, NGT Dinh, L Lazzarotto, Effects of lubricant and lubrication parameters on friction during hot steel forging, International Journal of Material Forming 1 (1), 2008, 1223–1226CrossRef

Titel: Friction Analysis in Bulk Metal Forming
verfasst von: Laurent Dubar
André Dubois
Mirentxu Dubar
Verlag: Springer Berlin Heidelberg
Buch: 60 Excellent Inventions in Metal Forming
Print ISBN: 978-3-662-46311-6

Electronic ISBN: 978-3-662-46312-3

Copyright-Jahr: 2015
DOI: https://doi.org/10.1007/978-3-662-46312-3_4

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht